Growth of InAs Quantum Dots on Germanium Substrate Using Metal Organic Chemical Vapor Deposition Technique
نویسندگان
چکیده
Self-assembled InAs quantum dots (QDs) were grown on germanium substrates by metal organic chemical vapor deposition technique. Effects of growth temperature and InAs coverage on the size, density, and height of quantum dots were investigated. Growth temperature was varied from 400 to 450 °C and InAs coverage was varied between 1.40 and 2.35 monolayers (MLs). The surface morphology and structural characteristics of the quantum dots analyzed by atomic force microscope revealed that the density of the InAs quantum dots first increased and then decreased with the amount of InAs coverage; whereas density decreased with increase in growth temperature. It was observed that the size and height of InAs quantum dots increased with increase in both temperature and InAs coverage. The density of QDs was effectively controlled by growth temperature and InAs coverage on GaAs buffer layer.
منابع مشابه
InAs/GaAs quantum dots with wide-range tunable densities by simply varying V/III ratio using metal-organic chemical vapor deposition
The complicated behaviors of InAs/GaAs quantum dots with increasing V/III ratio associated with several competing mechanisms have been described. The results demonstrate that the densities of InAs quantum dots can be tuned in a wide range from 105 to 1010 cm-2 by simply manipulating V/III ratio via metal-organic chemical vapor deposition. These results are mainly ascribed to the changes of cove...
متن کاملSelective Growth of InAs Quantum Dots by Metalorganic Chemical Vapor Deposition
We report results of both strain-driven surface segregation of indium from InGaAs thin films as well as selective area epitaxy of InAs quantum dots using these films. InAs segregation from an underlying InGaAs film allows for preferential growth of quantum dots when additional InAs is deposited. By using standard lithography techniques, a two-step selective growth process for quantum dots is ac...
متن کاملMeasurement of electro-optic coefficients of 1.3 lm self-assembled InAs=GaAs quantum dots
The electro-optic properties of 1.3 mm self-assembled InAs=GaAs quantum dots grown by metal organic chemical vapour deposition are reported. The linear and quadratic electro-optic coefficients are 2.4 10 11 m=V and 3.2 10 18 m=V, respectively, which are significantly larger than those of GaAs bulk materials. Also, the linear electro-optic coefficient is almost comparable to that of lithium niob...
متن کاملModeling and characterization of InAs/GaAs quantum dot lasers grown using metal organic chemical vapor deposition
We report on the lasing characteristics of threeand five-stack InAs/GaAs quantum dot QD lasers grown by metal organic chemical vapor deposition. By increasing the number of stacked dot layers to 5, lasing was achieved from the ground state at 1135 nm for device lengths as short as 1.5 mm no reflectivity coatings . The unamplified spontaneous emission and Z ratio as a function of injection curre...
متن کامل