Bond Strength in Thermally Sprayed Gas Turbine Shafts
نویسندگان
چکیده
In this paper, the bond strength of thermal spray coatings in high speed shafts has been studied. The metallurgical and mechanical studies has been made on the coated samples and shaft using optical microscopy, scanning electron microscopy (SEM). Keywords—Thermal spray, Residual stress, Wear mechanism, HVOF, Gas compressor shafts
منابع مشابه
Residual Stresses in Thermally Sprayed Gas Turbine Components
In this paper, the residual stress of thermal spray coatings in gas turbine component by curvature method has been studied. The samples and shaft were coated by hard WC-12Co cermets using high velocity oxy fuel (HVOF) after preparation in same conditions. The curvature of coated samples was measured by using of coordinate measurement machine (CMM). The metallurgical and Tribological studies has...
متن کاملControl of Coating Properties of Abradable Seals by On-Line Process Diagnostics
The efficiency of gas turbines is highly dependent upon the clearance between compressor housing and rotating blades. Abradable seal coatings are employed to minimize the clearance and control the over-tip leakage by allowing the blade tips to cut into the coating and herewith implementing a method of self-adjustment. These coatings consist of a thermally sprayed multiphase material, comprising...
متن کاملThe Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings
Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...
متن کاملEffect of Surface Roughness Morphology on Bond Strength of Thermal Sprayed WC-10Co-4Cr Ceramic/Metal Coating
In this study, the effect of surface roughness and roughness morphology on the bond strength of WC-Co-Cr coatings has investigated. The three different surfaces morphology are use for this purpose. The first and tow samples sandblasted with alumina and silicon carbide respectively. Other sample no sandblasted before spraying process. The same WC-10Co-4Cr coating deposited on the substrates with...
متن کاملEffect of Surface Morphologies on the Isothermal Oxidation Behavior of MCrAlY Coatings Fabricated by High-velocity Oxyfuel Processes
In this study, the effect of surface morphologies on the isothermal oxidation behavior of MCrAlY coatings fabricated by high-velocity oxyfuel (HVOF) processes was investigated. To do so, free standing coatings with as-sprayed and polished surfaces were isothermally oxidized at 1050°C. The thickness of the bond coat was approximately 380μm. The Ra of the as-sprayed and polished surfaces were 6.4...
متن کامل