Low-Temperature Magnetic Properties of Nanometric Fe-Based Particles
نویسندگان
چکیده
Fe-based nanoparticles were prepared by laser-driven pyrolysis. The assynthesised powder consists of α-Fe and Fe3O4/γ-Fe2O3 nanoparticles embedded in a pyrolytic carbon matrix. The crystallite size of 1.8 nm for α-Fe was calculated using the Scherrer formula. The as-synthesised nanopowder was superparamagnetic. The maximum of the zero-field cooling curve was observed at 32 K and the distribution of blocking temperatures g(TB) peaked at 11 K. As a result of small particle sizes and the soft matrix, the Lamb–Mössbauer factor f was significantly higher at 4 K than at 293 K.
منابع مشابه
Hydrothermal Synthesis of an Ethiodol Based Ferrofluid as a Potential MRI Contrast Agent
In the present work, stable ferrofluids containing oleic acid capped magnetite nanoparticles were synthesized via low temperature hydrothermal method. The physical and chemical properties of the synthesized particles were studied using TEM, XRD, AFM, VSM and PCS techniques. Mean particles size of the samples was between 4.5 and 10 nanometers, depending on experimental conditions. Effect ...
متن کاملMorphological and magnetic properties of superparamagnetic carbon-coated Fe nanoparticles produced by arc discharge.
Spherical carbon coated iron particles of nanometric diameter in the 5-10 nm range have been produced by arc discharge at near-atmospheric pressure conditions (using 5-8 x 10(4) Pa of He). The particles exhibit a crystalline dense iron core with an average diameter of 7.4 +/- 2.0 nm surrounded by a sealed carbon shell, shown by transmission electron microscopy (TEM), selected-area diffraction (...
متن کاملMagnetic and Temperature-Sensitive Composite Polymer Particles and Adsorption Behavior of Emulsifiers and Trypsin
A combination of magnetic and temperature-responsive properties in the same polymer composites is expected to increase their potential applications in the biomedical field. Accordingly, micron-sized magnetite/polystyrene/poly(2-dimethylaminoethyl methacrylate-ethyleneglycol dimethacrylate), which are abbreviated as Fe 3 O 4 /PS/P (DM-EGDM) composite polymer particles, were prepared by the seede...
متن کاملSynthesis and Magnetic Properties of Maghemite (γ-Fe2O3) Short-Nanotubes
We report a rational synthesis of maghemite (gamma-Fe(2)O(3)) short-nanotubes (SNTs) by a convenient hydrothermal method and subsequent annealing process. The structure, shape, and magnetic properties of the SNTs were investigated. Room-temperature and low-temperature magnetic measurements show that the as-fabricated gamma-Fe(2)O(3) SNTs are ferromagnetic, and its coercivity is nonzero when the...
متن کاملGrowth of CNTs over Fe–Co/Nanometric TiO2 Catalyst by CVD: The Effects of Catalyst Composition and Growth Temperature
In this research carbon nanotubes were produced by chemical vapor deposition of acetylene over a mixture of iron and cobalt catalysts supported on nanometric TiO2 and the influences of two synthesis parameters: growth temperature and catalyst composition ratio on properties of end-product carbon nanotubes were investigated. The catalytic basis was prepared by wet impregnation ...
متن کامل