An Investigation of Degradation of Mechanical Behaviour of Prestressing Strands Subjected to Chloride Attacking
نویسنده
چکیده
Corrosion of reinforcing and prestressing steel due to chloride contamination is one of the primary causes of deterioration of concrete structures. A review of published literatures shows that the research on the deterioration of mechanical properties of reinforcing steel is more than that on prestressing strands, even though the corrosion of prestressing strands may trigger structural collapse without warnings due to higher stress levels in the steel. This paper aims to investigate the degradation of mechanical behaviour of corroded prestressing strands. Details of a comprehensive experiment designed to examine the mechanical behaviour of corroded prestressing strands in concrete structural members are presented. A micromechanical damage model for failure mechanism of corroded prestressing strands is proposed, and a model for damage factor is derived. Based on these models, a constitutive model for corroded prestressing strands is developed and verified with test results. It is found in the paper that both the strength and ductility of corroded prestressing strands decrease with the increase of corrosion and that the hemispherical model for the pit shape is more appropriate for the prediction of strength reduction of corroded prestressing strands. The paper concludes that the constitutive model developed in the paper can be used to predict the mechanical behaviour of corroded prestressing strands accurately, paving the way for the assessment of corrosion-induced flexural failure of prestressed concrete structures.
منابع مشابه
Pull-Out Strength and Bond Behavior of Prestressing Strands in Prestressed Self-Consolidating Concrete
With the extensive use of self-consolidating concrete (SCC) worldwide, it is important to ensure that such concrete can secure uniform in-situ mechanical properties that are similar to those obtained with properly consolidated concrete of conventional fluidity. Ensuring proper stability of SCC is essential to enhance the uniformity of in-situ mechanical properties, including bond to embedded re...
متن کاملOptimization of Electromagnetic Acoustic Transducers (EMATs) for Condition Assessment of Civil Infrastructure
There are more than 130,000 prestressed concrete bridges in the United States with about 37,000 bridges being more than 30 years old. Prestressing steel strands are an important construction element used in these bridges and are critical to their performance. Presently there is no effective Nondestructive Evaluation (NDE) technology for condition assessment of these prestressing strands once th...
متن کامل2686: Investigation of Stress Corrosion Cracking Susceptibility of High Strength Stainless Steels for Use as Strand Material in Prestressed Concrete Construction in a Marine Environment
Stainless steel reinforcing has an elevated chloride threshold and is an attractive alternative for prestressed concrete applications. However, due to the high strength requirements for prestressing strands, concern exists about the possibility of stress corrosion cracking (SCC). This investigation screened for potential SCC development three candidate high strength alloys for use as prestresse...
متن کاملCorrosion Performance of Prestressing Strands in Contact with Dissimilar Grouts
To improve the corrosion protection provided to prestressing strands, anti-bleed grouts are used to fill voids in post-tensioning ducts that result from bleeding and shrinkage of older portland cement grouts. Environmental differences caused by exposing the strands to dissimilar grouts, however, have the potential to cause rapid corrosion. Portland cement grout, gypsum grout, and four commercia...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کامل