Improving Nanofiber Membrane Characteristics and Membrane Distillation Performance of Heat-Pressed Membranes via Annealing Post-Treatment
نویسندگان
چکیده
Electrospun membranes are gaining interest for use in membrane distillation (MD) due to their high porosity and interconnected pore structure; however, they are still susceptible to wetting during MD operation because of their relatively low liquid entry pressure (LEP). In this study, post-treatment had been applied to improve the LEP, as well as its permeation and salt rejection efficiency. The post-treatment included two continuous procedures: heat-pressing and annealing. In this study, annealing was applied on the membranes that had been heat-pressed. It was found that annealing improved the MD performance as the average flux reached 35 L/m2·h or LMH (>10% improvement of the ones without annealing) while still maintaining 99.99% salt rejection. Further tests on LEP, contact angle, and pore size distribution explain the improvement due to annealing well. Fourier transform infrared spectroscopy and X-ray diffraction analyses of the membranes showed that there was an increase in the crystallinity of the polyvinylidene fluoride-co-hexafluoropropylene (PVDF-HFP) membrane; also, peaks indicating the α phase of polyvinylidene fluoride (PVDF) became noticeable after annealing, indicating some β and amorphous states of polymer were converted into the α phase. The changes were favorable for membrane distillation as the non-polar α phase of PVDF reduces the dipolar attraction force between the membrane and water molecules, and the increase in crystallinity would result in higher thermal stability. The present results indicate the positive effect of the heat-press followed by an annealing post-treatment on the membrane characteristics and MD performance.
منابع مشابه
Progress of Membrane Engineering for Water Treatment
Together with the supply of energy and the environmental protection, fresh water is one of the three keys elements for the sustainable development of every society. Where the availability of water cannot be carried out by using conventional sources, unavoidable appears the resort of the major water source: the sea. Today, RO is one the most used membrane processes for the production of fresh wa...
متن کاملArt to use Electrospun Nanofbers/Nanofber Based Membrane in Waste Water Treatment, Chiral Separation and Desalination
The technique to fabricate nanofibrous mat by electro-spinning has been known for a long time. But the attempts to use the electospun nanofiber mats, also known as electro-spun nanofiber membranes (ENMs), for filtration purposes began only recently. Among many membrane filtration processes, air cleaning by the removal of dust particles has already been commercialized and the product has been in...
متن کاملOn Designing of Membrane Thickness and Thermal Conductivity for Large Scale Membrane Distillation Modules
Membrane distillation has the potential to concentrate solutions to their saturation level, thus offering the possibility to recover valuable salts from the solutions. The process performance and stability, however, is strongly dependent upon the features of membranes applied. In addition, several other parameters, membrane thickness and thermal conductivity significantly affect the process per...
متن کاملCarbon membranes for gas separation processes: Recent progress and future perspective
Carbon membrane can be produced using a wide variety of polymer precursor materials via heat treatment process. A general concept route of precursor selection-preparation-modification-performance analysis platform for the carbon membrane has been proposed to promote the development of carbon membrane material for a wide range of application. The current review considers the recent progress of c...
متن کاملPerformance of Chemically Modified TiO2-poly (vinylidene fluoride) DCMD for Nutrient Isolation and Its Antifouling Properties
The surface properties of TiO2-PVDF nanocomposite membranes were investigated by incorporating different chemically modified TiO2 nanoparticles into the poly (vinylidene fluoride) (PVDF) matrix. The nanocomposite membranes were prepared via dual coagulation bath diffusion and the induced phase inversion method. The membrane surface morphologies were investigated by using SEM and AFM and related...