Similar sealability between bioceramic putty ready-to-use repair cement and white MTA.
نویسندگان
چکیده
This study was designed to assess the ability to prevent glucose penetration of a bioceramic putty ready-to-use repair cement comparing to white mineral trioxide aggregate (WMTA). After root canal instrumentation, the apical 3 mm of maxillary incisors were resected and root-end cavities with depth of 3 mm were prepared with ultrasound and filled with the tested materials (15 roots per group). All roots were mounted in a double chamber system to assess glucose penetration using 15 psi pressure application. After 1 h, glucose concentrations in the lower chamber were measured following an enzymatic reaction. Four roots were used as controls. The Mann-Whitney test verified differences in glucose leakage between groups and the Tukey's test was used for multiple comparisons. Significance level was set at 5%. There was no significant difference in glucose leakage between iRoot BP Plus and White MTA groups. iRoot BP Plus had a similar ability to that of white MTA in preventing glucose leakage as a root-end filling material.
منابع مشابه
Physical properties and hydration behavior of a fast-setting bioceramic endodontic material
BACKGROUND To investigate the physical properties and the hydration behaviour of the fast-setting bioceramic iRoot FS Fast Set Root Repair Material (iRoot FS) and three other endodontic cements. METHODS iRoot FS, Endosequence Root Repair Material Putty (ERRM Putty), gray and white mineral trioxide aggregate (G-MTA & W-MTA), and intermediate restorative material (IRM) were evaluated. The setti...
متن کاملبررسی هیستولوژیک ترمیم پرفوریشنهای مکانیکی ناحیه فورکیشن دندانهای پرهمولر سگ با استفاده از MTA خاکستری، MTA سفید و سمان پرتلند
Background and Aim: Furcal perforation has a great impact on prognosis of endodontic treatments, requiring immediate and proper intervention. Gray MTA is applied as material of choice in repairing perforations. The aim of this study was to evaluate the repair of mechanical furcal perforations, histologically using white MTA and Portland cement and compare them with gray MTA. Materials and Metho...
متن کاملComparison of the root-end seal provided by bioceramic repair cements and White MTA.
AIM To compare the ability of Ceramicrete, BioAggregate and white ProRoot MTA (mineral trioxide aggregate) to prevent glucose leakage through root-end fillings. METHODOLOGY After root canal instrumentation, the apical 3 mm of maxillary incisors were resected and retropreparations, 3 mm in depth, were created with ultrasound. Root-end cavities were filled with the tested materials (15 roots pe...
متن کاملEffect of Blood Exposure on Push-Out Bond Strength of Four Calcium Silicate Based Cements
INTRODUCTION The purpose of this study was to compare the push-out bond strength of white ProRoot Mineral Trioxide Aggregate (MTA), Biodentine, calcium-enriched mixture (CEM) cement and Endosequence Root Repair Material (ERRM) putty after exposure to blood. METHODS AND MATERIALS A total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...
متن کاملAnalysis of radiopacity, pH and cytotoxicity of a new bioceramic material
OBJECTIVE RetroMTA® is a new hydraulic bioceramic indicated for pulp capping, perforations or root resorption repair, apexification and apical surgery. The aim of this study was to compare the radiopacity, pH variation and cytotoxicity of this material to ProRoot® MTA. MATERIAL AND METHODS Mixed cements were exposed to a digital x-ray along with an aluminum stepwedge for the radiopacity assay...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Brazilian dental journal
دوره 24 4 شماره
صفحات -
تاریخ انتشار 2013