Characterization of a Low Shrinkage Dental Composite Containing Bismethylene Spiroorthocarbonate Expanding Monomer
نویسندگان
چکیده
In this study, a novel dental composite based on the unsaturated bismethylene spiroorthocarbonate expanding monomer 3,9-dimethylene-1,3,5,7-tetraoxa-spiro[5,5]undecane (BMSOC) and bisphenol-S-bis(3-meth acrylate-2-hydroxypropyl)ether (BisS-GMA) was prepared. CQ (camphorquinone) of 1 wt % and DMAEMA (2-(dimethylamino)ethyl methacrylate) of 2 wt % were used in a photoinitiation system to initiate the copolymerization of the matrix resins. Distilled water contact angle measurements were performed for the wettability measurement. Degree of conversion, volumetric shrinkage, contraction stress and compressive strength were measured using Fourier Transformation Infrared-FTIR spectroscopy, the AccuVol and a universal testing machine, respectively. Within the limitations of this study, it can be concluded that the resin composites modified by bismethylene spiroorthocarbonate and BisS-GMA showed a low volumetric shrinkage at 1.25% and a higher contact angle. The lower contraction stress, higher degree of conversion and compressive strength of the novel dental composites were also observed.
منابع مشابه
Low-shrinkage composite for dental application.
In modern research, development of monomers that reduce shrinkage of composite materials remains an ongoing quest and perennial challenge. The purpose of this study, therefore, was to analyze the shrinkage behaviour of an innovative composite material for dental restorations based on a monomer with a new chemical formulation, known as silorane. To this end, shrinkage stress development during c...
متن کاملRelationship between polymerization shrinkage of matrix-monomers and marginal leakage of composite resins.
The intimate marginal adaptation of composite resins is considered to be the most important requisite, and this is strongly influenced by polymerization shrinkage, thermal expansion or mechanical properties of the resins. The highly loaded composite resins, developed recently have yielded good results on thermal expansion and mechanical properties. Consequently, little attention has been paid t...
متن کاملCharacteristics of Dental Restorative Composite Resins Prepared from 2,2-bis-[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane Derivatives and Spiro Orthocarbonate
To reduce volumetric shrinkage of the commercially available polymeric dental composite during curing reaction, (2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane) (bis-GMA) derivatives, i.e., (2,2-bis[3-methyl, 4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propan) (DMBis-GMA) and (2,2bis[3,5-dimethyl, 4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane) (TMBis-GMA) were sy...
متن کاملEffect of low shrinkage monomers on physicochemical properties of dental resin composites.
UNLABELLED The aim of this study was to evaluate the effect of low shrinkage monomers on physicochemical properties of dental resin composites. Two low shrinkage resin composites: one with a crosslink branching monomer (Kalore, GC Corp) and a novel monomer (Venus Diamond, Heraeus Kulzer) were compared to a conventional resin composite formulation (Filtek Z250, 3M/ESPE). The volumetric shrinkage...
متن کاملConversion, shrinkage, water sorption, flexural strength and modulus of re-mineralizing dental composites.
OBJECTIVES Cure, volumetric changes and mechanical properties were assessed for new dental composites containing chlorhexidine (CHX) and reactive calcium phosphate-containing (CaP) to reduce recurrent caries. METHODS 20wt.% of light curable urethane dimethacrylate based liquid was mixed with 80wt.% glass filler containing 10wt.% CHX and 0-40wt.% CaP. Conversion versus depth with 20 or 40s lig...