Comparative Study of Electroless Copper Film on Different Self-Assembled Monolayers Modified ABS Substrate

نویسندگان

  • Jiushuai Xu
  • Ruibin Fan
  • Jiaolong Wang
  • Mengke Jia
  • Xuanrui Xiong
  • Fang Wang
چکیده

Copper films were grown on (3-Mercaptopropyl)trimethoxysilane (MPTMS), (3-Aminopropyl)triethoxysilane (APTES) and 6-(3-(triethoxysilyl)propylamino)-1,3,5- triazine-2,4-dithiol monosodium (TES) self-assembled monolayers (SAMs) modified acrylonitrile-butadiene-styrene (ABS) substrate via electroless copper plating. The copper films were examined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). Their individual deposition rate and contact angle were also investigated to compare the properties of SAMs and electroless copper films. The results indicated that the formation of copper nuclei on the TES-SAMs modified ABS substrate was faster than those on the MPTMS-SAMs and APTES-SAMs modified ABS substrate. SEM images revealed that the copper film on TES-SAM modified ABS substrate was smooth and uniform, and the density of copper nuclei was much higher. Compared with that of TES-SAMs modified resin, the coverage of copper nuclei on MPTMS and APTES modified ABS substrate was very limited and the copper particle size was too big. The adhesion property test demonstrated that all the SAMs enhanced the interfacial interaction between copper plating and ABS substrate. XRD analysis showed that the copper film deposited on SAM-modified ABS substrate had a structure with Cu(111) preferred orientation, and the copper film deposited on TES-SAMs modified ABS substrate is better than that deposited on MPTMS-SAMs or APTES-SAMs modified ABS resins in electromigrtion resistance.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Seedless micropatterning of copper by electroless deposition on self-assembled monolayers

A novel approach for direct electroless (EL) patterning of copper films without catalysts has been developed. In a special electroless solution employed in the present study, the formation of copper particles was observed and the negatively charged surfaces were confirmed by zeta potential measurements. The conditions of the solution (ionic strength, pH, temperature, additives etc.) greatly aff...

متن کامل

Patterned Self-Assembled Monolayers Formed by Microcontact Printing Direct Selective Metalization by Chemical Vapor Deposition on Planar and Nonplanar Substrates

Self-assembled monolayers (SAMs) of alkylsiloxanes were patterned by microcontact printing @CP) on a number of substrates: A1/A1&, SUSi02, TiN/Ti02, glasses, indium tin oxide (ITO), and plasma-modified polyimide. The patterned SAMs on these surfaces define and direct the selective chemical vapor deposition (CVD) of copper using (hexafluoroacetylacetonato)(vinyltrimethylsilane)copper(I) (CuI(hfa...

متن کامل

Fabrication of new carbon paste electrodes based on gold nano-particles self-assembled to mercapto compounds as suitable ionophores for potentiometric determination of Copper ions

In the present study, we investigate the potentiometric behavior of Cu2+ carbon paste electrodes based on two mercapto compounds 2-Ethylmino-5-Mercapto-1,3,4-Thiadiazole (EAMT) and 2-Acetylamino-5-mercapto-1,3,4-thiadiazole (AAMT) self-assembled on gold nano-paricle (GNP) as ionophore. Then, the results obtained from the modified electrodes are compared. The self-assembled ionophores exhibit a ...

متن کامل

Is Due Principally to Electrons

This paper models damage induced by monochromatized Al Ka X-rays to organic thin films using self-assembled monolayers supported on Al, Ti, Cu, and Au. An X-ray photoelectron spectrometer is used both to conduct the X-ray irradiation and to analyze the damage. In all cases these monolayers comprised a trifluoroacetimido (CF3CONH-) group bound to the substrate through an undecyl tether to either...

متن کامل

Selective Metallization of Cured Su-8 Microstructures Using Electroless Plating Method

In this talk, we report a research work on fabrication and metallization of high aspect ratio polymer microstructures fabricated using UV lithography of SU-8 on silicon substrate. Electroless plating of metal film on both the top and sidewall surfaces of microstructures were achieved while the silicon substrate was not plated. The primary chemical mechanisms and possible applications were also ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 15  شماره 

صفحات  -

تاریخ انتشار 2014