MAGNETIC PROPERTIES OF AMORPHOUS Fe-Ti ALLOYS PRODUCED BY FACING TARGET TYPE SPUTTERING
نویسندگان
چکیده
In bulk FeTi alloys prepared by facing target type sputtering, an amorphous phase was obtained between 25 and 75 at% Ti. These alloys are weak itinerant electron ferromagnets and the Curie temperature decreases with increasing Ti concentration and becomes zero at about 60 at% Ti.
منابع مشابه
Magnetic Properties of Pr–Fe–Al Alloys Produced by the Metallic Mold Casting Method
The structures and magnetic properties of Pr–Fe–Al alloys produced by the metallic mold casting method were investigated. The Pr–Fe–Al alloy consisted of the amorphous phase together with the non-ferromagnetic Pr phase. Magnetic measurements confirmed that the origin of coercivity in the alloys was the amorphous phase. It was found that the Curie temperature and coercivity of the alloys were st...
متن کاملLarge variation of magnetic properties of amorphous Fe–Zr thin films with Ar pressure during sputtering
A large change is observed in the magnetic properties of amorphous Fe-Zr thin films sputtered at different Ar pressures. The change depends on the composition of the alloys and at compositions near 60 at.% Fe, for example, the magnetisation measured at 10 kOe increases 30-fold with an increase in the Ar pressure from 2 to 10 mTorr. The magnetic properties are well explained by a combination of ...
متن کاملارزیابی ریزساختاری و خواص مغناطیسی آلیاژ آمورف پایه کبالت Co70B20Si5Fe4Mo1 تولید شده بهروش مذابریسی و آلیاژسازی مکانیکی
Cobalt-based amorphous alloys attracted the attention of many researchers to carry out fundamental research for their application in electronics, sensors and magnetic memory due to their special magnetic properties including close to zero Magnetostriction, magnetic permeability and high saturation magnetization. The purpose of this study is the formation and evaluation of microstruct...
متن کاملHITPERM soft-magnetic underlayers for perpendicular thin film media
A class of nanocrystalline alloys, HITPERM ~Fe, Co!–M–B–Cu (M5Zr,Hf,Nb, etc.! found to exhibit excellent soft-magnetic properties is being studied for use as a soft-magnetic underlayer for perpendicular recording media. Previously, we reported that HITPERM films of ;100 nm thickness sputtered at room temperature ~RT! and at ;2.3 W/cm power density had exhibited an amorphous microstructure, whic...
متن کاملEffect of Ni on Amorphization of Ti-Cu-Ni Ternary alloys Prepared by Mechanical alloying
Amorphous alloys has been taken into consideration because of their unique properties and are nominated as the future engineering materials. In this research, the effect of Ni and milling time on amorphization process and thermal stability of Ti50Cu50-xNix(x=10, 15, 25 at%) alloy system were investigated. The evolution of amorphization during milling, thermal stability and subsequent heat treat...
متن کامل