Structural and magnetic properties of epitaxial La0.67Sr0.33MnO3 films and nanostructures
نویسنده
چکیده
No part of this work may be reproduced by print, photocopy or any other means without the permission in writing from the publisher. Cover page illustration: Front side; Three-dimensional AFM images of LSMO nanowires of different dimensions on STO substrates. Top one is having width 422nm, height 26nm and periodicity 600nm, left one is having width 292nm height 25nm and periodicity 600nm, and right one is having width 146nm, height 43nm and periodicity 600nm. Back side; Three-dimensional AFM image of LSMO nano dots of diameter 300nm, height 44nm and periodicity 600nm.
منابع مشابه
Effect of Cobalt Concentration on Structural and Magnetic Properties of Co-Fe Thin Films
Co-Fe films were electrodeposited on Cu substrate from electrolytes with different Co concentration levels. X-ray diffraction (XRD) was used to investigate the films crystal structures. The results indicate that if the Co concentration is less that the Fe concentration, the cubic structure appears in the films, while the hexagonal structure dominates when the C...
متن کاملStrain-induced symmetry reduction of epitaxial La0.67Sr0.33MnO3 films
Introduction Due to spin, lattice and orbital coupling, manganese-based La1-xSrxMnO3 (LSMO) compounds exhibit unusual physical properties, such as colossal magnetoresistance and almost total spin polarization (95% at 4 K) at the composition x = 0.33 [1]. Thus, La0.67Sr0.33MnO3 has significant potential for applications in spintronic devices such as magnetic field sensors, networked environmenta...
متن کاملUltraviolet detectors based on annealed zinc oxide thin films: epitaxial growth and physical characterizations
In this report, ultraviolet (UV) detectors were fabricated based on zinc oxide thin films. The epitaxial growth of zinc oxide thin films was carried out on bare glass substrate with preferred orientation to (002) plane of wurtzite structure through radio frequency sputtering technique. The structural properties indicated a dominant peak at 2θ=34.28º which was matched with JCPDS reference card N...
متن کاملThickness dependent magnetotransport in ultra-thin manganite films
To understand the near-interface magnetism in manganites, uniform, ultrathin films of La0.67Sr0.33MnO3 were grown epitaxially on single crystal (001) LaAlO3 and (110) NdGaO3 substrates. The temperature and magnetic field dependent film resistance is used to probe the film’s structural and magnetic properties. A surface and/or interface related dead-layer is inferred from the thickness dependent...
متن کاملIn situ magnetic a.nd structural analysis of epitaxial NisoFezo thin films for spin-valve heterostructures
We have investigated structural and magnetic properties of epitaxial (100) N&Feel0 films grown on relaxed Cu/Si(lOO) seed layers. The crystallographic texture and orientation of these films was analyzed in situ by reflection high energy electron diffraction (RHEED), and M situ by x-ray diffraction and cross-sectional transmission electron microscopy (XTEM). In particular, RHEED intensities were...