The Influence of Silicon Content on Recrystallization of Twin-Roll Cast Aluminum Alloys for Heat Exchangers
نویسندگان
چکیده
منابع مشابه
TEM Investigation of Precipitation in Al-Mn Alloys with Addition of Zr
Aluminium and its alloys belong to the most widely used metallic materials for industrial applications. One of the possible casting methods is twin-roll casting which produces sheets with high solid solution supersaturation. Decomposition of this supersaturated material during heat treatment was studied in aluminium alloys from the AW-3003 series – one standard grade and the other modified by a...
متن کاملLocalized Recrystallization in Cast Al-Si-Mg Alloy During Solution Heat Treatment: Dilatometric and Calorimetric Studies
During heat treatment, the work piece experiences a range of heating rates depending upon the sizes and types of furnace. When the Al-Si-Mg cast alloy is heated to the solutionizing temperature , recrystallization takes place during the ramp-up stage. The effect of heating rate on recrystallization in the A356 (Al-Si-Mg) alloy was studied using dilatometric and calorimetric methods. Recrystalli...
متن کاملAnnealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding
Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mecha...
متن کاملInvestigation of the Microstructure Evolution and Deformation Mechanisms of a Mg-Zn-Zr-RE Twin-Roll-Cast Magnesium Sheet by In-Situ Experimental Techniques
Twin roll casting (TRC), with a relatively fast solidification rate, is an excellent production method with promising potential for producing wrought semi or final Mg alloy products that can often suffer from poor formability. We investigate in this study the effect of the TRC method and the subsequent heat treatment on the microstructure and deformation mechanisms in Mg-Zn-Zr-Nd alloy deformed...
متن کاملThe Effect of Artificial Aging Treatment and Lubrication Modes on the Cutting Force and the Chip Surface Morphology when Drilling Al-Si-Mg (A356) Cast Alloys
This article reports the effects of various artificial aging methods and lubrication modes (dry, mist, wet) on the recorded cutting forces and chip morphology in drilling Al-Si-Mg (A356) cast alloys. In the course of this work, the work part sampled were as-received alloy (T0), solution heat-treated alloy (SHT) and then aged alloys at 155°C, 180°C, and 220°C (T4, T6, T61, T7), respectively. The...