Behavior of Cu-WC-Ti Metal Composite Afterusing Planetary Ball Milling
نویسندگان
چکیده
Copper based composites reinforced with WC and Ti particles were prepared using planetary ball-mill. The experiment was designed by using Taguchi technique and milling was carried out in an air for several hours. The powder was characterized before and after milling using the SEM, TEM and X-ray for microstructure and for possible new phases. Microstructures show that milled particles size and reduction in particle size depend on many parameters. The distance d between planes of atoms estimated from X-ray powder diffraction data and TEM image. X-ray diffraction patterns of the milled powder did not show clearly any new peak or energy shift, but the TEM images show a significant change in crystalline structure of corporate on titanium in the composites. Keywords—ball milling, microstructures, titanium, tungsten carbides, X-ray
منابع مشابه
Mechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite
In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite p...
متن کاملEffect of processing parameters on the mechano-chemical synthesis of nano crystalline Mo-Cu/Al2O3 composite
In this study, molybdenum-copper/alumina nano composite was synthesized with mechano-chemical method using high energy planetary ball milling. The molybdenum oxide, copper oxide and aluminum powder were used as starting materials and reaction appeared to occur through a rapid combustion reaction process. The evaluation of powder particles after different milling times was studied by X-ray diffr...
متن کاملWear Behavior in Micro and Nano-Structured WC-9Co-0.7VC Cemented Carbide Produced by Rapid Hot Press Sintering
The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...
متن کاملInfluence of Micron-Ti and Nano-Cu Additions on the Microstructure and Mechanical Properties of Pure Magnesium
In this study, metallic elements that have limited/negligible solubility in pure magnesium (Mg) were incorporated in Mg using the disintegrated melt deposition technique. The metallic elements added include: (i) micron sized titanium (Ti) particulates with negligible solubility; (ii) nano sized copper (Cu) particulates with limited solubility; and (iii) the combination of micro-Ti and nano-Cu. ...
متن کاملEFFECT OF COMPOSITION AND MILLING TIME ON THE SYNTHESIS OF NANOSTRUCTURED Ni-Cu ALLOYS BY MECHANICAL ALLOYING METHOD
Ni and Cu elemental powder mixtures containing 25, 50, and 75% at Cu were subjected to mechanical alloying in a planetary ball mill under various milling times. Structural evolution was analyzed by means of X-ray diffraction and scanning electron microscopy. Experimental results indicated that nanostructured solid solution alloy powders having homogeneous distribution of Ni and Cu were formed b...
متن کامل