176 . Effect of selective Co addition on magnetic properties of Nd 2 ( FeCo ) 14 B / ? - Fe nanocomposite magnets
نویسندگان
چکیده
searching existing data sources, gathering and maintaining the data needed, and completing and reviewing the collection of information. Send comments regarding this burden estimate or any other aspect of this collection of information, including suggesstions for reducing this burden, to Washington Headquarters Services, Directorate for Information Operations and Reports, 1215 Jefferson Davis Highway, Suite 1204, Arlington VA, 22202-4302. Respondents should be aware that notwithstanding any other provision of law, no person shall be subject to any oenalty for failing to comply with a collection of information if it does not display a currently valid OMB control number. PLEASE DO NOT RETURN YOUR FORM TO THE ABOVE ADDRESS.
منابع مشابه
RAPID COMMUNICATION Nanocomposite (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer magnets with high performance
The structural and magnetic properties of rare-earth nanocomposite magnets of a (Nd,Dy)(Fe,Co,Nb,B)5.5 single layer and a (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer prepared by sputtering and heat treatment have been investigated. Incomplete exchange coupling behaviour is observed in the Ti-buffered NdDyFeCoNbB + 40 wt%Fe single layer magnet. After annealing, the laminated nanostructure consisting ...
متن کاملEffect of selective Co addition on magnetic properties of Nd2(FeCo)14B/-Fe nanocomposite magnets
Nd2Fe14B/α-Fe-based hard/soft nanocomposite magnets with Co addition have been prepared by ball-milling and warm compaction. It was found that Co addition into the magnetically hard phase improves magnetic properties significantly, especially the remanence ratio and coercivity. The effect on the magnetic properties of the selective Co addition may be attributed to enhanced interdiffusion across...
متن کاملEffect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کامل176 . Effect of selective Co addition on magnetic properties of Nd 2 ( FeCo ) 14 B / ? - Fe nanocomposite
searching existing data sources, gathering and maintaining the data needed, and completing and reviewing the collection of information. Send comments regarding this burden estimate or any other aspect of this collection of information, including suggesstions for reducing this burden, to Washington Headquarters Services, Directorate for Information Operations and Reports, 1215 Jefferson Davis Hi...
متن کاملINFLUENCE OF HEATING RATE ON MICROSTRUCTURE AND MAGNETIC PROPERTIES OF Fe3B/Nd2Fe14B NANOCOMPOSITE MAGNETS
The nanocomposite magnet, which is composed of exchange coupled nanocrystalline soft (Fe3B, α-Fe) and hard (Nd2Fe14B) magnetic phases, was first reported by Coehoorn et al. [1], and the theoretical basis of it was reported by Kneller and Hawig [2]. Nd-Fe-B based nanocomposite magnet has attracted considerable research interest due to its excellent magnetic properties with relatively low amount ...