Crystal structure and magnetic properties of LaCa0.143 (4)O0.857 (4)F0.143 (4)Bi0.857 (4)S2
نویسندگان
چکیده
The synthesis, structure, and magnetic properties of lithium dibarium calcium oxide fluoride di-sulfide are reported. LaCa0.143 (4)O0.857 (4)F0.143 (4)Bi0.857 (4)S2 crystallizes in the tetra-gonal space group P4/nmm. The structure exhibits disorder of the Ca(2+) and Bi(3+) cations, and the O(2-) and F(-) anions. The structure is composed of a stacking of [(O,F)2La2] layers and double [(Bi,Ca)S2] layers. Magnetic property measurements indicate a very small magnetization at 300 K and the existence of weak ferromagnetism at 2 K.
منابع مشابه
Low Temperature Hydrothermal Synthesis and Characterization and Optical Properties of Sr5Nb4O15 – Nb2O5 Nanocomposite
Sr5Nb4O15 – Nb2O5 nanocomposites were synthesized in 2 and 4 M KOH aqueous solutions, via a non-stoichiometric 1:2 Sr:Nb molar ratio hydrothermal method at 160°C for 48 h (S1 and S2, respectively). Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-Ray diffraction (PXRD) technique. It was found that Sr5Nb4O15 has been crystallized in hexa...
متن کاملEffect of Magnetic Field on Surface Morphology and Magnetic Properties of FeCu/Cu Nano layers Prepared by Electrodeposition Technique: Investigation of Magneto-hydrodynamic Effect
In this paper, the effect of magnetic field on the morphology, structure and magnetic properties of electrodeposited FeCu/Cu thin films was investigated. The films were deposited on Au2PdAg/glass substrates using electrodeposition technique in potentiostatic control. The magnetic fields of 5000 and 7000 Oe were applied on deposition bath during deposition. Two series of thin films were prepared...
متن کاملLow Temperature Hydrothermal Synthesis and Characterization and Optical Properties of Sr5Nb4O15 – Nb2O5 Nanocomposite
Sr5Nb4O15 – Nb2O5 nanocomposites were synthesized in 2 and 4 M KOH aqueous solutions, via a non-stoichiometric 1:2 Sr:Nb molar ratio hydrothermal method at 160°C for 48 h (S1 and S2, respectively). Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-Ray diffraction (PXRD) technique. It was found that Sr5Nb4O15 has been crystallized in hexa...
متن کاملA Pair of Manganese(III) Schiff-Base Enantiomers: Synthesis, Crystal Structure and Magnetic Characterization
Based-on the quasi-planar tetra-dentate Schiff-base ligand, a pair of manganese(III) Schiff-base enantiomers formulated as {[Mn(R,R-3-MeOSalcy)(H2O)(CH3OH)]ClO4}2 (1) and {[Mn(S,S-3-MeOSalcy)(H2O)(CH3OH)]ClO4}2 (2) (3-MeOSalcy = N,N′-(1,2-cyclohexanediylethylene)bis(3-methoxysalicylideneiminato)dianion) ...
متن کاملPhysical and Magnetic Properties Comparison of Cobalt Ferrite Nanopowder Using Sol-gel and Sonochemical Methods
Cobalt ferrite or CoFe2O4 has unique physical and magnetic properties depend on its synthesis method. The application of cobalt ferrite as nanomedicine material become more interesting, however analysis on physical and magnetic properties based on synthesis method have not been discussed. The cobalt ferrite in this research was synthesised using two different methods: the ...
متن کامل