Hydrothermal synthesis of NiWO4 crystals for high performance non-enzymatic glucose biosensors
نویسندگان
چکیده
A facile hydrothermal route for the synthesis of ordered NiWO4 nanocrystals, which show promising applications as high performance non-enzymatic glucose sensor is reported. The NiWO4-modified electrodes showed excellent sensitivity (269.6 μA mM(-1 )cm(-2)) and low detection limit (0.18 μM) for detection of glucose with desirable selectivity, stability, and tolerance to interference, rendering their prospective applications as cost-effective, enzyme-free glucose sensors.
منابع مشابه
Facile Synthesis and Electrochemical Performance of Graphene-Modified Cu2O Nanocomposite for Use in Enzyme-Free Glucose Biosensor
Graphene-modified Cu2O nanocomposite was synthesized under facile microwave irradiation of an aqueous solution and has been investigated as an enzyme-free glucose biosensor. Morphology and crystal structure of the graphene-modified Cu2O nanocomposite were investigated by using electron microscopy and X-Ray Diffraction (XRD) analyses. Also, the electrochemical performan...
متن کاملNon-Enzymatic Glucose Sensor Composed of Carbon-Coated Nano-Zinc Oxide
Nowadays glucose detection is of great importance in the fields of biological, environmental, and clinical analyzes. In this research, we report a zinc oxide (ZnO) nanorod powder surface-coated with carbon material for non-enzymatic glucose sensor applications through a hydrothermal process and chemical vapor deposition method. A series of tests, including crystallinity analysis, microstructure...
متن کاملNano-sized AlPO4-5 Crystals: Synthesis and characterization
Molecular sieves and zeolites are materials whose crystalline frameworks form nanometer or subnanometer pores. A variety of different crystal structures are known having a range of pore sizes. Because the pore sizes are usually smaller than 2 nm, they are classified as microporous materials. Synthesis of microporous materials is usually conducted by the high temperature treatment (80-200 °C) of...
متن کاملNano-sized AlPO4-5 Crystals: Synthesis and characterization
Molecular sieves and zeolites are materials whose crystalline frameworks form nanometer or subnanometer pores. A variety of different crystal structures are known having a range of pore sizes. Because the pore sizes are usually smaller than 2 nm, they are classified as microporous materials. Synthesis of microporous materials is usually conducted by the high temperature treatment (80-200 °C) of...
متن کاملLow Temperature Hydrothermal Synthesis and Characterization and Optical Properties of Sr5Nb4O15 – Nb2O5 Nanocomposite
Sr5Nb4O15 – Nb2O5 nanocomposites were synthesized in 2 and 4 M KOH aqueous solutions, via a non-stoichiometric 1:2 Sr:Nb molar ratio hydrothermal method at 160°C for 48 h (S1 and S2, respectively). Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-Ray diffraction (PXRD) technique. It was found that Sr5Nb4O15 has been crystallized in hexa...
متن کامل