Reduced Impedance and Superconductivity of SnAgCu Solder Alloy at High Frequency
نویسندگان
چکیده
Skin effect of lead-free solder joints is investigated over a wide frequency band. Contrary to common believe that ‘effective impedance of solder alloys increases with frequency’, resistance tends to saturate when frequency reaches a critical value, 10 MHz for SAC solder alloys. Negative surface impedance growth rate is observed when employs square waveform AC current loading at high current density. Further increased frequency causes a dramatic reduction of effective resistance. At 11 MHz with current density of 106 A/cm2, effective resistance of solder alloy drops to near zero value.
منابع مشابه
Electromigration in Solder Joints and Solder Lines
Au (0.05 μm) 69.4 μm Electromigration may affect the reliability of flip-chip solder joints. Eutectic solder is a two-phase alloy, so its electromigration behavior is different from that in aluminum or copper interconnects. In addition, a flipchip solder joint has a built-in currentcrowding configuration to enhance electromigration failure. To better understand electromigration in SnPb and lead...
متن کاملHigh Melting Lead-Free Mixed BiAgX Solder Paste System
Although lead-free soldering has been main stream in the industry since 2006 with the replacement of the eutectic SnPb system by the SnAgCu system, the development of drop-in lead-free alternatives for high melting high lead solder alloys is still far from mature. The BiAg alloy exhibits acceptable bulk strength, but very poor ductility and wetting. Therefore, it is not acceptable as an option....
متن کاملEffects of solder volume on formation and redeposition of Au- containing intermetallics in Au/Ni-SnAgCu-Ni(P) solder joints
SnAgCu is one of the most promising candidates for lead-free solders to replace conventional eutectic SnPb solders. The effects of solder volume on interfacial reactions and microstructure evolution in Au/Ni-SnAgCu-Ni(P) solder joints have been investigated under soldering and thermal aging conditions. The results show that solder volume has a strong effect on the formation of Au-containing int...
متن کاملEffects of Solder Volume on Formation and Redeposition of Au-Containing Intermetallics in Ni/Au-SnAgCu-Ni(P) Solder Joints
SnAgCu is one of the most promising candidates for lead-free solders to replace conventional eutectic SnPb solders. The effects of solder volume on interfacial reactions and microstructure evolution in Ni/Au-SnAgCu-Ni(P) solder joints have been investigated under soldering and thermal aging conditions. The results show that solder volume has a strong effect on the formation of Au-containing int...
متن کاملEffects of process conditions on reliability, microstructure evolution and failure modes of SnAgCu solder joints
In this study, microstructure evolution at intermetallic interfaces in SnAgCu solder joints of an area array component was investigated at various stages of a thermal cycling test. Failure modes of solder joints were analyzed to determine the effects of process conditions on crack propagation. Lead-free printed-circuit-board (PCB) assemblies were carried out using different foot print designs o...
متن کامل