Phase separation and nanostructuring in the thermoelectric material PbTe1−xSx studied using the atomic pair distribution function technique

The average and local structures of the PbTe 1−x PbS x system of thermoelectric materials has been studied using the Rietveld and atomic pair distribution function methods. Samples with 0.25 x are macroscopically phase separated. Phase separation was suppressed in a quenched x=0.5 sample which, nonetheless, exhibited a partial spinodal decomposition. The promising thermoelectric material with x=0.16 showed intermediate behavior. Combining TEM and bulk scattering data suggests that the sample is a mixture of PbTe-rich material and a partially spinodally decomposed phase similar to the quenched 50% sample. This confirms that, in the bulk, this sample is inhomogeneous on a nanometer length scale, which may account for its enhanced thermoelectric figure of merit.