Tailoring the grooved texture of electrospun polystyrene nanofibers by controlling the solvent system and relative humidity

نویسندگان

  • Wanjun Liu
  • Chen Huang
  • Xiangyu Jin
چکیده

In this study, we have successfully fabricated electrospun polystyrene (PS) nanofibers having a diameter of 326 ± 50 nm with a parallel grooved texture using a mixed solvent of tetrahydrofuran (THF) and N,N-dimethylformamide (DMF). We discovered that solvent system, solution concentration, and relative humidity were the three key factors to the formation of grooved texture and the diameter of nanofibers. We demonstrated that grooved nanofibers with desired properties (e.g., different numbers of grooves, widths between two adjacent grooves, and depths of grooves) could be electrospun under certain conditions. When THF/DMF ratio was higher than 2:1, the formation mechanism of single grooved texture should be attributed to the formation of voids on the jet surface at the early stage of electrospinning and subsequent elongation and solidification of the voids into a line surface structure. When THF/DMF ratio was 1:1, the formation mechanism of grooved texture should be ascribed to the formation of wrinkled surface on the jet surface at the early stage of electrospinning and subsequent elongation into a grooved texture. Such findings can serve as guidelines for the preparation of grooved nanofibers with desired secondary morphology.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Electrospinning of Grooved Polystyrene Fibers: Effect of Solvent Systems

Secondary surface texture is of great significance to morphological variety and further expands the application areas of electrospun nanofibers. This paper presents the possibility of directly electrospinning grooved polystyrene (PS) fibers using both single and binary solvent systems. Solvents were classified as low boiling point solvent (LBPS): dichloromethane (DCM), acetone (ACE), and tetrah...

متن کامل

Electrospun Nitrocellulose and Composite Nanofibers

Electrospinning was applied to nitrocellulose (NC) solutions  in DMF, DMSO  and  Ethyl  methyl  keton  to  obtain  NC  nanofibers. Electrospraying  process  was  observed  when  DMF  was  used  as solvent.  In  comparison  to NC/DMF, NC/DMSO  solution  resulted  in the  formation  of  a  coating  film  as  indicate  by  SEM.  Two  different electrospun  nanofibers,  smooth  nanofibers  wit...

متن کامل

Preparation of N, N-dichloropolystyrene sulfonamide nanofiber as a regenerable self-decontaminating material for protection against chemical warfare agents

N,N-dichloropolystyrene sulfonamide as a decontaminant was synthesized in 5 steps from styrene monomer. Styrene was first polymerized. Then, sulfonation reaction was performed by H2SO4 (c) followed by chlorination with POCl3 obtain chlorosulfonated polystyrene. Amidification reaction was then applied to get sulfonamide resin. Sulfonamide resin was treat...

متن کامل

Preparation of N, N-dichloropolystyrene sulfonamide nanofiber as a regenerable self-decontaminating material for protection against chemical warfare agents

N,N-dichloropolystyrene sulfonamide as a decontaminant was synthesized in 5 steps from styrene monomer. Styrene was first polymerized. Then, sulfonation reaction was performed by H2SO4 (c) followed by chlorination with POCl3 obtain chlorosulfonated polystyrene. Amidification reaction was then applied to get sulfonamide resin. Sulfonamide resin was treat...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 9  شماره 

صفحات  -

تاریخ انتشار 2014