Composites prepared from the waterborne polyurethane cationomers-modified graphene. Part II. Electrical properties of the polyurethane films
نویسندگان
چکیده
The research was planned to test electrical properties of polymer films made from polyurethane cationomers with 0-2 wt.% graphene admixture. The cationomers were synthetized in the reaction of 4,4'-methylenebis(phenyl isocyanate), polycaprolactone diol (M = 2000), N-methyldiethanolamine, and formic acid. It was found that addition of approx. 2 wt.% of graphene causes the loss of volume resistivity by three orders of magnitude and percolation threshold is already set at approx. 1 wt.%. The frequency characteristic of a real part of permittivity ε' and imaginary part of permittivity ε″ were measured for the tested films. On the base of Havriliak-Negami equation, parameters of relaxation functions in frequency domain were estimated for samples containing various contents of graphene. The influence of the cationomer phase structure on observed changes of dielectric losses coefficient tgδ in the full-measuring frequency spectrum was discussed.
منابع مشابه
Composites prepared from the waterborne polyurethane cationomers—modified graphene. Part I. Synthesis, structure, and physicochemical properties
In the reaction of 4,4'-methylenebis(phenyl isocyanate), polycaprolactone diol, and N-methyldiethanolamine, they were synthesized aqueous dispersions of polyurethane cationomers, from which films were prepared after adding 0-2 wt% graphene. In order to obtain nanocomposites, graphene was previously noncovalent functionalized in tetrahydrofurane in the field of ultrasound. The chemical structure...
متن کاملMechanical Properties and Wear Resistance of Sulfonated Graphene/Waterborne Polyurethane Composites Prepared by In Situ Method
In order to improve the dispensability of graphene oxide (GO) in waterborne polyurethane (WPU), sulfonated graphene (SGO) with superior dispersity was prepared by modifying graphene oxide with sodium 2-chloroethane sulfonate to introduce hydrophilic sulfonic groups into the structure. SGO/WPU composites were prepared using isophorone diisocyanate (IPDI), polytetramethylene ether glycol (PTMEG 2...
متن کاملInvestigation of the synergistic effect of titania micro and nanoparticles on the hydrophobic properties of polyurethane composite coating
One of the ways to improve the performance of ceramic insulators in polluted climates is to use polymer coatings reinforced with ceramic particles. The purpose of this study is to compare the effect of adding Titania nanoparticles and Titania micro-nanoparticles on hydrophobic properties of PU. In this method, stearic acid, which is a cheap and environmentally friendly material, was used for su...
متن کاملFabrication and study of structural, optical and electrical properties of UV curable conductive polyurethane acrylate films containing polyaniline-Co3O4 nanocomposites
In this research, Novel UV curable conductive nanocomposites containing urethane acrylate and PANi-Co3O4 nanocomposite have been prepared. At first, PANi- Co3O4 nanocomposites have been synthesized and then PUA-PANi-Co3O4 nanocomposites films were prepared by ultraviolet radiation. UV-Vis and FT-IR studies confirm that there was strong chemical interaction between PANi and Co3O4 nanoparticles, ...
متن کاملEffect of nanozeolite 13X on thermal and mechanical properties of Polyurethane nanocomposite thin films
Polyurethane/zeolite 13X nanocomposite films were fabricated using solution casting method. The synthesized nanocomposite films were structurally characterized using SEM, TGA and tensile analysis. SEM images showed appropriate distribution of nanocrystalline zeolite particles within polyurethane matrix. Better thermal stability of nanocomposite films in comparison to neat polyurethane was shown...
متن کامل