The Bainite Reaction Kinetics in Austempered Ductile Iron
نویسنده
چکیده
Bainitic reaction kinetics in ductile iron contained according to Ukrainian standard (weight %) 3.603.80 carbon, 2.60-2.80 Si, 0.12 Mn, 0.60 Cu and additionally alloyed by Mo (0.15-0.20) has been studied. It was found that the overall transformation kinetics becomes slower as transformation temperature increase. This is because more intensive redistribution of carbon into austenite at higher temperatures. Two austenites wiith different carbon content have been fixed and kinetics of their lattices parameters has been studied.
منابع مشابه
Structural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملThe Bainitic Phase Transformation in Aluminium Containing Ductile Irons after Short Time of Austempering
The influence of aluminium on the microstructure of austempered ductile cast iron (ADI) has been studied. A number of irons of different compositions have been made by green sand casting and gravity die casting of appropriate design to provide the experimental materials. Austenitising was carried out at different temperatures and holding times for a variety of experimental irons to achieve suff...
متن کاملOptimizing the Microstructure and Mechanical Properties of Austempered Ductile Iron for Automobile Differential Gear
Austempered ductile iron (ADI) has been proved to be an excellent material as it possesses attractive properties: high strength, ductility and toughness combined with good wear resistance and machinability. These properties can be achieved upon adequate heat treatment which yields the optimum microstructure for a given chemical composition. The heat treating of the ductile cast iron produces th...
متن کاملEffect of Alloying Elements on the Microstructure and Mechanical Properties of Austempered Ductile Iron Alloys
متن کامل
Influence of Composition and Austempering Temperature on Machinability of Austempered Ductile Iron
Present investigations involve a systematic study on the machinability of austempered ductile irons (ADI) developed from four commercially viable ductile irons alloyed with different contents of 0, 0.1, 0.3 and 0.6 wt.% of Ni. The influence of Ni content, amount of retained austenite and hardness of ADI on machining behavior has been conducted systematically. Austempering heat treatment was car...
متن کامل