Process Chain for the Production of a Bimetal Component from Mg with a Complete Al Cladding

نویسندگان

  • Wolfgang Förster
  • Birgit Awiszus
چکیده

With respect to its density, magnesium (Mg) has a high potential for lightweight components. Nevertheless, the industrial application of Mg is limited due to, for example, its sensitivity to corrosion. To increase the applicability of Mg, a process chain for the production of a Mg component with a complete aluminum (Al) cladding is presented. Hydrostatic co-extrusion was used to produce bar-shaped rods with a diameter of 20 mm. The bonding between the materials was verified by ultrasonic testing. Specimens with a length of 79 mm were cut off from the rods and forged by using a two-staged process. After the first step (Heading), the Mg core was removed partially by drilling to ensure a complete enclosing of the remaining Mg during the second forging step (Net shape forging). The geometry of the drilling hole and the heading die design were dimensioned with the Finite Element-simulation software FORGE. Hence, a complete Al-enclosed Mg component was achieved by using the described process chain and forming processes. Microstructural investigations confirm the formation of an intermetallic interface as expected.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Punch plastic deformation pipe cladding (PPDPC) as a novel tube cladding method

This study presents a new mechanical tube cladding process named punch plastic deformation pipe cladding (PPDPC) based on local deformation by pressing a punch into the inner layer of the bimetal tube. To investigate the capability of the process, stainless steel tube (as the inner layer) is bonded to a carbon steel pipe (as the outer layer) to fabricate a bimetal pipe. Shear punch tests were u...

متن کامل

Investigation of ECAR Routes on Mechanical Properties of Explosive-Welded Al-Cu Bimetal

Equal channel angular rolling (ECAR) is a severe plastic deformation method that covered plastic deformation of sheets. In this study, effects of ECAR route shave been investigated on the mechanical and microstructure properties of explosive-welded Al-Cu bimetal. At first, the explosive welding process has been performed to prepare the Al-Cu bimetals. Then, to relieve the stress and preparing o...

متن کامل

Investigation of ECAR Routes on Mechanical Properties of Explosive-Welded Al-Cu Bimetal

Equal channel angular rolling (ECAR) is a severe plastic deformation method that covered plastic deformation of sheets. In this study, effects of ECAR route shave been investigated on the mechanical and microstructure properties of explosive-welded Al-Cu bimetal. At first, the explosive welding process has been performed to prepare the Al-Cu bimetals. Then, to relieve the stress and preparing o...

متن کامل

اثر نسبت حجمی مذاب- جامد و سرعت دوران بر فصل مشترک جفت فلزی منیزیم- آلومینیم در ریخته‌گری گریز از مرکز

In this study, centrifugal casting process was used for producing Al/Mg bimetal. Molten Mg was poured at 700 oC, with 1.5 and 3 melt-to-solid volume ratio (Vm/Vs) into the 450 oC preheated solid Al rotating at 800, 1200, 1600 and 2000 rpm. Castings were kept inside the centrifuged casting machine and cooled down to 150 oC. Investigating the effect of melt-to-solid volume ratio showed that incre...

متن کامل

An Experimental Study on the process parameters of Incremental Forming of Explosively-Welded Al/Cu Bimetal

Single point incremental sheet metal forming is a sheet metal forming process that forms products without the complex dies and tools with low cost. In this study, the incremental sheet metal forming process has been experimentally investigated on the explosively-welded Al/Cu bimetal sheets. Also, the effects of process parameters, such as arrangement of layer`s bimetal, tool diameter and tool p...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2018