Porous Copolymer Resins: Tuning Pore Structure and Surface Area with Non Reactive Porogens
نویسندگان
چکیده
In this review, the preparation of porous copolymer resin (PCR) materials via suspension polymerization with variable properties are described by tuning the polymerization reaction, using solvents which act as porogens, to yield microporous, mesoporous, and macroporous materials. The porogenic properties of solvents are related to traditional solubility parameters which yield significant changes in the surface area, porosity, pore volume, and morphology of the polymeric materials. The mutual solubility characteristics of the solvents, monomer units, and the polymeric resins contribute to the formation of porous materials with tunable pore structures and surface areas. The importance of the initiator solubility, surface effects, the temporal variation of solvent composition during polymerization, and temperature effects contribute to the variable physicochemical properties of the PCR materials. An improved understanding of the factors governing the mechanism of formation for PCR materials will contribute to the development and design of versatile materials with tunable properties for a wide range of technical applications.
منابع مشابه
Characterization of Pore Structure in Biologically Functional Poly(2-Hydroxyethyl Methacrylate) - Poly(Ethylene Glycol) Diacrylate (PHEMA-PEGDA)
A copolymer composed of poly(2-hydroxyethyl methacrylate) (PHEMA) and poly(ethylene glycol) diacrylate (PEGDA) (PHEMA-PEGDA) is structurally versatile. Its structure can be adjusted using the following porogens: water, sucrose, and benzyl alcohol. Using phase separation technique, a variety of surface architectures and pore morphologies were developed by adjusting porogen volume and type. The w...
متن کاملImpact of Porogens on the Pore Characteristics of Zirconia Particles Made by Polymer-Induced Colloid Aggregation
Zirconia particles were prepared from a 20% colloidal sol (ZrO2) by the polymerinduced colloid ag gregation (PICA) process, both in the presence and absence of porogens. Specifically, porous zirco nia particles having varying porosity were prepared by a twostep protocol wherein a porogen was first embedded during the particle synthesis, followed by its removal in a subsequent step. In this ...
متن کاملEffect of Candida antarctica lipase B immobilization on the porous structure of the carrier.
A series of poly(GMA-co-EGDMA) resins with identical composition but varying particle sizes, pore radii, specific surface areas and specific volumes are studied to assess how Candida antarctica lipase B immobilization affects the porosity of the copolymer particles. Mercury porosimetry reveals a significant change in the average pore size (up to 6.1-fold), the specific surface area (up to 3.2-f...
متن کاملThermal stabilization of alumina modified by lanthanum
Transition alumina, with different La loadings, were synthesized from boehmite (AlOOH) hydrosols containing a PEO/PPO/PEO triblock copolymer (Pluronics P123) and lanthanum nitrate. After calcination at 500 °C, the xerogels prepared from these sols have large specific surface area ( 400 m/g) and very large porous volumes, increasing with the amount of La to reach 2.5 cm/g for La/(La + Al) = 0.03...
متن کاملSyntheses of complex mesoporous silicas using mixtures of nonionic block copolymer surfactants: understanding formation of different structures using solubility parameters.
The use of block copolymer (BCP) nonionic surfactant mixtures (including Pluronic, Brij and Tetronic types) as templates for synthesizing porous silica materials of mixed pore sizes is explored here. These systems have important applications because combinations of pore sizes can allow rapid access of reactants (via large pores) whilst providing the very high surface area of small pores for hig...
متن کامل