Fatigue of micromachined stainless steel structural materials for vibrational energy harvesting
نویسندگان
چکیده
This work presents fatigue measurement for micromachined stainless steel (SUS304) structural substrate using resonant bending mode. Micromachined specimens for fatigue test had a cantilever structure with a proof mass. They were fabricated by FeCl3 wet etching and wire-discharged cutting. The SUS specimens had Young’s modulus of 198 GPa on average. The endurance limit of micromachined specimens was 213 MPa on average after 10 8 cycles under our fracture definition. The large SUS specimens had the endurance limit of 229 MPa after 10 7 cycles.
منابع مشابه
Energy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملCorrosion Fatigue of 17-4pH Stainless Steel in a Simulated Sea Water Solution
Since martensitic precipitation hardened 17-4pH stainless steel has been widely used in corrosive environments, evaluation of its corrosion fatigue behavior is important. In this research, after microstructural studies, mechanical, corrosion, fatigue and corrosion fatigue tests were performed on 17-4pH specimens. Fatigue and corrosion fatigue tests were carried out at the stress ratio of -1 an...
متن کاملThe combined effect of molybdenum and nitrogen on the fatigued microstructure of 316 type austenitic stainless steel
Introduction The mechanical properties of austenitic stainless steels, including the low cyclic fatigue behavior have been a subject of numerous studies [1-8]. Nitrogen addition, in general, increases the fatigue strength by decreasing the stacking fault energy of austenitic stainless steels [6]. The stacking fault energy has a strong influence on the cross slip difficulty, thus it affects the ...
متن کاملThe development of grain-orientation-dependent residual stressess in a cyclically deformed alloy.
There have been numerous efforts to understand and control the resistance of materials to fracture by repeated or cyclic stresses. The micromechanical behaviours, particularly the distributions of stresses on the scale of grain size during or after mechanical or electrical fatigue, are crucial to a full understanding of the damage mechanisms in these materials. Whether a large microstress devel...
متن کاملMonotonic and Cyclic J-integral Estimation for Through-Wall Cracked Straight Pipes
The evaluation of energy release rate and centre Crack Opening Displacement (COD) for circumferential Through-Wall Cracked (TWC) pipes is an important issue in the assessment of critical crack length for unstable fracture. The ability to predict crack growth continues to be an important component of research for several structural materials. Crack growth predictions can aid the understanding of...
متن کامل