Characterization of Environmentally Sustainable Resole Phenolic Resins Synthesized with Plant-based Bioresources
نویسندگان
چکیده
“Green” resole phenolic resins for laminating applications were synthesized, and their properties and thermal stability were determined. The plant-based cardanol and condensed tannin were used as the partial substitutes of up to 40% of the phenol in the synthesis of the phenolic resins. The resins were synthesized with different proportions of phenol (P) to cardanol (C) and with different total molar ratio to the formaldehyde (F) in the resins (1.25 to 2.0). An increased cardanol content resulted in a proportional increase in the flexibility and fracture toughness of the cured cardanol-phenol-formaldehyde (CPF) resins. Also, a direct proportionality was found between increasing cardanol content and decreased crosslink density of the CPF resins. The best results were obtained with the formulation with a P:F molar ratio equal to 1:1.25. Tannin was incorporated into the CPF resins and the fracture toughness and flexibility values of the cured Tannin-CPF resins were found to be proportional to and increasing with the tannin content. However, glass transition temperature (Tg), flexural stress, and flexural modulus values of the CPF resins decreased with the tannin content. TGA-FTIR study of the resins was carried out and the emitted gas species during the pyrolysis of the samples were identified. The thermal stability and the temperature of degradation of the cured CPF resins decreased with increasing cardanol content.
منابع مشابه
Thermal Curing Behavior and Tensile Properties of Resole Phenol-Formaldehyde Resin/Clay/Cellulose Nanocomposite*
This study investigated the effects of layered clay on the thermal curing behavior and tensile properties of resole phenol-formaldehyde (PF) resin/clay/cellulose nanocomposites. The thermal curing behavior of the nanocomposite was characterized using conventional differential scanning calorimetry (DSC) and temperature modulated (TMDSC). The addition of clay was found to accelerate resin curing,...
متن کاملThe green synthesis of gold nanoparticle using extract of Virola oleifera
Background The green synthesis consists of an environmentally friendly method of producing gold nanoparticles (AuNP’s). Physical and chemical syntheses have energy intensive and may involve toxic chemicals, while biological techniques are cost-effective, clean, non-toxic and environmentally appropriate. Virola oleifera is widely used in folk medicine. The bark of the trunk when scraped produce ...
متن کاملNeutron scattering, electron microscopy and dynamic mechanical studies of carbon nanofiber/phenolic resin composites
Carbon nanofiber (CNF)/resole phenolic resin (Hitco 134A) composites exhibited very large increases of bending storage modulus above the glass transition temperature and had higher glass transition temperatures with increasing CNF weight percentage. Small angle neutron scattering (SANS) from dilute suspensions of surface-oxidized CNF in D2O exhibited a Guinier plateau in the q range examined, i...
متن کاملManufacturing and Characterization of Composite Fibreboards with Posidonia oceanica Wastes with an Environmentally-Friendly Binder from Epoxy Resin
Highly environmentally-friendly fibreboards were manufactured by hot-press moulding using Posidonia ocaeanica wastes and a partially biobased epoxy resin as binder. Fibreboards with a constant fibre content of 70 wt % were successfully manufactured by thermo-compression. The effects of a conventional alkali treatment were compared to the synergistic effects that additional silanization with two...
متن کامل