Nanodiamond crystals containing single color centers have been grown by chemical vapor deposition (CVD). The fluorescence from individual crystallites was directly correlated with crystallite size using a combined atomic force and scanning confocal fluorescence microscope. Under the conditions employed, the optimal size for single optically active nitrogen-vacancy (NV) center incorporation was measured to be 60 to 70 nm. The findings highlight a strong dependence of NV incorporation on crystal size, particularly with crystals less than 50 nm in size.
منابع مشابه
Single nitrogen vacancy centers in chemical vapor deposited diamond nanocrystals.
Nanodiamond crystals containing single color centers have been grown by chemical vapor deposition (CVD). The fluorescence from individual crystallites was directly correlated with crystallite size using a combined atomic force and scanning confocal fluorescence microscope. Under the conditions employed, the optimal size for single optically active nitrogen-vacancy (NV) center incorporation was ...
متن کاملDiamond nanophotonics
We demonstrate the coupling of single color centers in diamond to plasmonic and dielectric photonic structures to realize novel nanophotonic devices. Nanometer spatial control in the creation of single color centers in diamond is achieved by implantation of nitrogen atoms through high-aspect-ratio channels in a mica mask. Enhanced broadband single-photon emission is demonstrated by coupling nit...
متن کاملScalable fabrication of high purity diamond nanocrystals with long-spin-coherence nitrogen vacancy centers.
The combination of long spin coherence time and nanoscale size has made nitrogen vacancy (NV) centers in nanodiamonds the subject of much interest for quantum information and sensing applications. However, currently available high-pressure high-temperature (HPHT) nanodiamonds have a high concentration of paramagnetic impurities that limit their spin coherence time to the order of microseconds, ...
متن کاملEnhanced optical properties of chemical vapor deposited single crystal diamond by low-pressure/high-temperature annealing.
Single crystal diamond produced by chemical vapor deposition (CVD) at very high growth rates (up to 150 microm/h) has been successfully annealed without graphitization at temperatures up to 2200 degrees C and pressures <300 torr. Crystals were annealed in a hydrogen environment by using microwave plasma techniques for periods of time ranging from a fraction of minute to a few hours. This low-pr...