Focused ion beam induced deposition: fabrication of three-dimensional microstructures and Young’s modulus of the deposited material
نویسنده
چکیده
In this work, some of the possibilities of focused ion beams for applications in microsystem technology are explored. Unlike most previous studies, the emphasis is on ‘additive’ techniques, i.e. localized maskless deposition of metals and insulators. More precisely, we will show the possibility of fabricating small three-dimensional structures, using focused ion beam deposition of silicon oxide. Deposition examples will show that the technique is most promising for small post-processing steps or prototyping, because of its high degree of flexibility. Furthermore, an investigation into the mechanical properties of the deposited material is presented. More specifically, the Young’s modulus of the deposited silicon oxide is determined.
منابع مشابه
NANO EXPRESS Berkovich Nanoindentation on AlN Thin Films
Berkovich nanoindentation-induced mechanical deformation mechanisms of AlN thin films have been investigated by using atomic force microscopy (AFM) and cross-sectional transmission electron microscopy (XTEM) techniques. AlN thin films are deposited on the metalorganic chemical-vapor deposition (MOCVD) derived Si-doped (2 9 10 cm) GaN template by using the helicon sputtering system. The XTEM sam...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کاملBending, Buckling and Vibration of a Functionally Graded Porous Beam Using Finite Elements
This study presents the effect of porosity on mechanical behaviors of a power distribution functionally graded beam. The Euler-Bernoulli beam is assumed to describe the kinematic relations and constitutive equations. Because of technical problems, particle size shapes and micro-voids are created during the fabrication which should be taken into consideration. Two porosity models are proposed. T...
متن کاملMechanical Property Measurement of 0.5mm CMOS Microstructures
Measurements are reported on the mechanical properties of high-aspect-ratio micromechanical structures formed using a conventional 0.5-μm CMOS process. Composite structures are etched out of the CMOS dielectric, aluminum, and gate-polysilicon thin films using a post-CMOS CHF3:O2 reactive-ion etch and followed by a SF6:O2 silicon etch for release. Microstructures have a height of 5 μm and beam w...
متن کامل3D Microfabrication Using Emulsion Mask Grayscale Photolithography Technique
Recently, the rapid development of technology such as biochips, microfluidic, micro-optical devices and micro-electromechanical-systems (MEMS) demands the capability to create complex design of three-dimensional (3D) microstructures. In order to create 3D microstructures, the traditional photolithography process often requires multiple photomasks to form 3D pattern from several stacked photores...
متن کامل