Test Plan to Update SRS HLW Tank Material Properties Database by Determining Synergistic Effects of Dynamic Strain Aging and Stress Corrosion Cracking (U)
نویسنده
چکیده
منابع مشابه
Strategic Research: In-Tank Generation of Corrosion Inhibitors
Government nor any agency thereof, nor any of their employees, makes any warranty, express or implied, or assumes any legal liability or responsibility for the accuracy, completeness, or usefulness of any information, apparatus, product or process disclosed, or represents that its use would not infringe privately owned rights. Reference herein to any specific commercial product, process or serv...
متن کاملStress Corrosion Cracking Detection of Sensitized Stainless Steel 304 in Chloride Media by Using Electrochemical Impedance Spectroscopy (EIS)
Electrochemical impedance spectroscopy (EIS) was used to detect stress corrosion cracking (SCC) in stainless steel 304 alloy exposed to an aqueous environment at 120 °C. Stainless steel 304 alloy as u-bend was tested in the solution that contains 40 weight percent of magnesium chloride. U-bended samples were prepared according to ASTM G30. EIS measurements were always performed simultaneously o...
متن کاملDynamic Strain Ageing and Eac of Deformed Nitrogen-alloyed Aisi 316 Stainless Steels
Intergranular stress corrosion cracking has occurred in BWR environments in non-sensitised, cold-worked austenitic stainless steel materials. The affecting parameters are so far not fully known, but deformation mechanisms may be decisive. The effect of cold deformation and nitrogen content on the deformation behaviour of austenitic stainless steels was investigated. The materials were austeniti...
متن کاملStudy of the Corrosion Resistance of Austenitic Stainless Steels during Conversion of Waste to Biofuel
The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens eithe...
متن کاملA Monitoring Method Based on FBG for Concrete Corrosion Cracking
Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology ...