Synthesis, Crystal Structure and Nonlinear Optical Property of RbHgI3
نویسندگان
چکیده
Searching for new nonlinear optical (NLO) crystals to be used in the infrared (IR) region is still a challenge. This paper presents the synthesis, crystal structure and properties of a new halide, RbHgI3. Its non-centrosymmetric single crystal can be grown in solution. In its crystal structure, all the polar [HgI4] groups align in such a way that brings a favorable net polarization. The measurement by Kurtz–Perry powder technique indicates that RbHgI3 shows a phase-matchable second harmonic generation (SHG) property seven times stronger than that of KH2PO4 (KDP). RbHgI3 displays excellent transparency in the range of 0.48–25 μm with relatively good thermal stability. The UV absorption implies that this yellow compound’s band gap is about 2.56 eV, close to that of AgGaS2. A preliminary measurement indicates that the laser-induced damage threshold of the crystal is about 28.3 MW/cm2. These preliminary experimental data reveal that RbHgI3 is a new candidate as nonlinear optical material in the infrared region.
منابع مشابه
Low temperature hydrothermal synthesis, characterization and optical properties of Sr6Nb10O30 – Nb2O5 nanocomposite
Sr6Nb10O30–Nb2O5 nanocomposite was synthesized in 2M NaOH aqueous solution. A stoichiometric 1:1 Sr:Nb molar ratio hydrothermal method at 120°C was used to synthesize this nanocomposite. Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-ray diffraction (PXRD) technique. It was found that Sr6Nb10O30 was crystallized in tetragonal crystal ...
متن کاملLow temperature hydrothermal synthesis, characterization and optical properties of Sr6Nb10O30 – Nb2O5 nanocomposite
Sr6Nb10O30–Nb2O5 nanocomposite was synthesized in 2M NaOH aqueous solution. A stoichiometric 1:1 Sr:Nb molar ratio hydrothermal method at 120°C was used to synthesize this nanocomposite. Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-ray diffraction (PXRD) technique. It was found that Sr6Nb10O30 was crystallized in tetragonal crystal ...
متن کاملSynthesis of BiVO4 nanoparticles by the co-precipitation method and study the crystal structure, optical and photocatalytic properties of them
In this paper, the bismuth vanadate (BiVO4) nanoparticles were synthesized at 600 °C calcination temperature by co-precipitation method. To study the crystal structure, morphology, optical and photocatalytic properties of the samples, the X-ray diffraction analysis, field emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, Fourier-transform infrared spectroscopy and ult...
متن کاملImprovement of Optical Properties in Hexagonal Index-guiding Photonic Crystal Fiber for Optical Communications
Waveguides with low confinement loss, low chromatic dispersion, and low nonlinear effects are used in optical communication systems. Optical fibers can also be employed in such systems. Besides optical fibers, photonic crystal fibers are also highly suitable transmission media for optical communication systems. In this paper, we introduce two new designs of index-guiding photonic crystal fiber ...
متن کاملLow Temperature Hydrothermal Synthesis and Characterization and Optical Properties of Sr5Nb4O15 – Nb2O5 Nanocomposite
Sr5Nb4O15 – Nb2O5 nanocomposites were synthesized in 2 and 4 M KOH aqueous solutions, via a non-stoichiometric 1:2 Sr:Nb molar ratio hydrothermal method at 160°C for 48 h (S1 and S2, respectively). Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-Ray diffraction (PXRD) technique. It was found that Sr5Nb4O15 has been crystallized in hexa...
متن کامل