Preparation and Upconversion Emission Modification of Crystalline Colloidal Arrays and Rare Earth Fluoride Microcrystal Composites
نویسندگان
چکیده
In this paper, highly ordered crystalline colloidal arrays containing rare earth fluoride microcrystals were fabricated. The upconversion emission property of rare earth fluoride microcrystals in crystalline colloidal arrays was studied and modified. A significant suppression and enhancement of the upconversion emission from the rare earth fluorides can be observed in the regions of the photonic band gap and its band edge, respectively. The suppression or enhancement factor was shown to be related to the ordered degree of the crystalline colloidal arrays and is critical in the preparation of upconversion displays and low-threshold lasers.
منابع مشابه
Upconversion properties of a transparent Er3þ–Yb3þ co-doped LaF3–SiO2 glass-ceramics prepared by sol–gel method
Transparent 0.1ErF3–0.1YbF3–5LaF3–94.8SiO2 (mol%) glass-ceramics was prepared by sol–gel method. Efficient upconversion emissions at 379, 407, 450, 490, 520, 540 and 660 nm were observed under 973 nm excitation. The signal at 379 nm is only 4.5 times weaker than the signal at 520 nm, that is readily visible by the naked eyes even with a pump power of 27 mW, indicating that this sample is a very...
متن کاملUnraveling Epitaxial Habits in the NaLnF4 System for Color Multiplexing at the Single-Particle Level.
We report an epitaxial growth technique for scalable production of hybrid sodium rare-earth fluoride (NaLnF4 ) microcrystals, including NaYF4 , NaYbF4 , and NaLuF4 material systems. The single crystalline nature of the as-synthesized products makes them strong upconversion emission. The freedom of combining a lanthanide activator (Er(3+) or Tm(3+) ) with a sensitizer (Yb(3+) ) at various doping...
متن کاملSequential Growth of Uniform β-NaYF4@β-NaLnF4 (Ln = Y, Lu, Yb) Microcrystals with Luminescent Properties of Multicolor Tuning and Dual-Mode Emission
We synthesized the uniform core-shell microstructured compounds with hexagonal phase NaYF₄:Er/Yb microrods as the core and hexagonal phase NaLnF₄ (NaYbF₄, NaLuF₄:Yb/Tm, NaYF₄:Yb/Er, NaYF₄:Eu) as the shell based on the hydrothermal reaction. These microscale core-shell structures provided a platform for the spatially confining optical process while possessing high luminescence efficiency. The th...
متن کاملRare Earth Ion-Doped Upconversion Nanocrystals: Synthesis and Surface Modification
The unique luminescent properties exhibited by rare earth ion-doped upconversion nanocrystals (UCNPs), such as long lifetime, narrow emission line, high color purity, and high resistance to photobleaching, have made them widely used in many areas, including but not limited to high-resolution displays, new-generation information technology, optical communication, bioimaging, and therapy. However...
متن کاملControlled synthesis, formation mechanism, and great enhancement of red upconversion luminescence of NaYF4:Yb3+, Er3+ nanocrystals/submicroplates at low doping level.
Strong red upconversion luminescence of rare-earth ions doped in nanocrystals is desirable for the biological/biomedical applications. In this paper, we describe the great enhancement of red upconversion emission (4F9/2 --> I15/2 transition of Er3+ ion) in NaYF4:Yb3+, Er3+ nanocrystals at low doping level, which is ascribed to the effectiveness of the multiphonon relaxation process due to the e...
متن کامل