Ohmic-Rectifying Conversion of Ni Contacts on ZnO and the Possible Determination of ZnO Thin Film Surface Polarity
نویسندگان
چکیده
The current-voltage characteristics of Ni contacts with the surfaces of ZnO thin films as well as single crystal (0001) ZnO substrate are investigated. The ZnO thin film shows a conversion from Ohmic to rectifying behavior when annealed at 800°C. Similar findings are also found on the Zn-polar surface of (0001) ZnO. The O-polar surface, however, only shows Ohmic behavior before and after annealing. The rectifying behavior observed on the Zn-polar and ZnO thin film surfaces is associated with the formation of nickel zinc oxide (Ni1-xZnxO, where x = 0.1, 0.2). The current-voltage characteristics suggest that a p-n junction is formed by Ni1-xZnxO (which is believed to be p-type) and ZnO (which is intrinsically n-type). The rectifying behavior for the ZnO thin film as a result of annealing suggests that its surface is Zn-terminated. Current-voltage measurements could possibly be used to determine the surface polarity of ZnO thin films.
منابع مشابه
Investigation of post-annealing effect on efficient ohmic contact to ZnO thin film using Ti/Al metallization strategy
Ohmic and Schottky contacts are playing a major role in the field of ZnO based electronics device fabrication. It is seen that several works have been reported on metallization scheme, contacts with this semiconducting material. But, the thickness of semiconducting material and the choosing of substrate still remain imperfect and inefficient for advanced IC technology. To estimate contact resis...
متن کاملStudies on ZnO/Si Heterojunction Diode Grown by Atomic Layer Deposition Technique
In this paper studies on Si/ZnO heterojunction diode is presented. In this work Zinc oxide (ZnO) was conformally deposited on Silicon (Si) Wafer by atomic layer deposition (ALD) technique without using a buffer layer. For low-temperature ALD deposition, diethyl zinc (DEZn) and deionized (DI) water were used as the sources for zinc and oxygen respectively. Surface characterization and optical ch...
متن کاملDetermination of the polarity of ZnO thin films by electron energy-loss spectroscopy
The polarity of the ZnO film grown on sapphire using an ultra-thin Ga wetting layer has been investigated by electron energyloss spectroscopy (EELS). The intensity of the oxygen K-edge in electron energy-loss spectrum from the ZnO film shows a prominent difference when the film orientation changes from the (0002) Bragg condition to the (0002̄) Bragg condition. The EELS study reveals that the ZnO...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کامل