Structural evolution in the graphitization process of activated carbon by high-pressure sintering
نویسندگان
چکیده
Activated carbon was treated at 5 GPa up to 1600 C, and the structural evolution in the graphitization process was investigated. The graphitization temperature is equal to 1200 C at 5 GPa, reflected by X-ray diffraction (XRD) patterns. Honeycomb-like structures in micron scale come into being in the high-pressure sintering temperature range of 100
منابع مشابه
Synthesis of TiC-Al2O3 Nanocomposite from Impure TiO2 by Mechanical Activated Sintering
In this research, the production possibility of TiC-Al2O3 nanocomposite, as a useful ceramic from commercially pure TiO2, aluminum powder and carbon black has been investigated. Routile (TiO2) with carbon black and aluminum were placed in a high energy ball mill and sampled during different milling times. Then, the activated powders were synthesized at different temperatures in an atmosphere co...
متن کاملThermodynamical Studies of Irreversible Sorption of CO2 by Wyodak Coal
Differential scanning calorimetry (DSC), temperature programmed desorption mass spectrometry (TPD-MS) and small angle neutron scattering (SANS) were used to investigate CO2 uptake by the Wyodak coal. Adsorption of carbon dioxide on Wyodak coal was studied by DSC. The exotherms evident at low temperatures are associated with the uptake of CO2 suggesting that carbon diox...
متن کاملModification of activated carbon by cold plasma and its effect on the adsorption of toluene
Abstract Background and aims: Clean air is one of the basic needs for human health and well-being. However, along with economic growth and development, transportation, urbanization and energy consumption have also risen and provide many concerns such as air pollution, which require urgent and wide attention. Air pollution in the worldwide is considered as a risk factor for human health and one...
متن کاملSpark Plasma Sintering of Ultra-High Temperature Tantalum/Hafnium Carbides Composite
TaC and HfC are thought to have the highest melting point (~4000°C) among all refractory materials. The binary solid solution of TaC and HfC (Ta4HfC5) is also considered as the most refractory material with the melting point over 4000 °C and valuable physical and mechanical properties. The main goal of this work is to fabricate TaC/HfCbased composites which consolidated by means of spark plasma...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کامل