Synthesis and Characterization of the Copolymer of Dodecyl Methacrylate/Styrene Containing an Amidine Functional Group
نویسندگان
چکیده
A copolymer of dodecyl methacrylate/styrene (DMA/St) containing the amidine functionality was synthesized and characterized. The one-step solution copolymerization process was carried out using a mixed solvent, high temperature, and a functional azo initiator, 2,2 -azobis[N,N -dimethylene isobutyramidine]. Copolymers with different compositions (DMA/St 10/1 to 1/2), molecular weight (Mn 2000–9000), and functionality (1.0–2.0) were prepared and characterized by NMR, FTIR, DSC, and elemental analysis. The molecular weight of the copolymers could be controlled by the amount of the initiators. Copolymer composition depends on the feed molar ratio of comonomers. The amidine functionality of the copolymers was determined by elemental analysis. It was found that 72% of the polymer chain has one functionality. The Tg of the copolymer depends on the feed molar ratio. This copolymer could be used as a potential dispersant for lubricant oil. © 2002 Wiley Periodicals, Inc.* J Appl Polym Sci 86: 1684–1691, 2002
منابع مشابه
Synthesis and Characterization of Acrylic Copolymers of 4-Chloromethyl Styrene with Incorporation of Phthalimide Groups and Amination of Resulted Polymers
4-ChloroMethyl Styrene (CMS) was copolymerized with different monomers such as Methyl MethAcrylate (MMA), Methyl Acrylate (MA), 2-EthylHexyl Acrylate (EHA) by free radical polymerization method at 70 ±1°C using a,a'-Azobis(IsoButyroNitrile) (AIBN) as an initiator. The copolymer compositions were obtained using related 1HNMR spectra and the poly...
متن کاملA Novel Initiator of [5-(benzyloxy)-4-oxo-4H-pyran-2-yl]methyl-2-bromo-2-methylpropanoateas in Atom Transfer Radical Polymerization of Styrene and Methyl Methacrylate
A novel nano-initiator containing kojic acid moiety, [5-(benzyloxy)-4-oxo-4H-pyran-2-yl)methyl-2-bromo-2-methylpropanoate was synthesized by the reaction of 5-(benzyloxy)-2-(hydroxymethyl)-4H-pyran-4-one with 2-bromoisobutyryl bromide in triethylamine and used as initiator in the atom transfer radical polymerization (ATRP) of styrene and methyl methacrylate in the presence of Cu(0)/CuCl2and N,N...
متن کاملSynthesis, Characterization and Thermal Stability Study of Styrene-based Ionomers I) Programmed Heating Experiments (10 oC/min to 500 oC)
Ionomers are generally described by copolymers having either acrylic or methacylic acid as one component and the other component is mostly either ethylene or styrene. The objective of this research was to study the thermal behaviour and stability of ionomers of styrene with some alkali metal acrylates. These materials have been synthesized by neutralization of the respective copoly...
متن کاملDenture base polymers, poly methyl methacrylate improved using free radical copolymerization
Poly methyl methacrylate (PMMA) is the most common material used in Prosthodontics. Several studies indicate a breakdown of the number of very high resin bases after 2 to 3 years to avoid breaking bass and several attempts have been made, such as altering the chemical structure of resin by adding causes cross linking or copolymerization. The innovative method for improving the physical properti...
متن کاملغشا کامپوزیتی برای غشای عبور پروتون پیل های سوختی بر اساس کوپلیمر متیل متا کریلات-مالایمید/ فسفوتنگستیک اسید
Poly(methyl methacrylate-co-nitrophenyl maleimide) (MMA-co-NMI) and poly(methyl methacrylate-co-hydroxyphenyl maleimide) (MMA-co-HMI) copolymers were synthesized using free radical polymerization of MMA with a new MI monomer containing phenyl and –NO2 groups. Proton exchange membrane fuel cell(PEMFC) were prepared using these copolymers as membrane matrix and phosphotungstic acid (PWA)...
متن کامل