A XAFS Study on the Site Determination of Additives in the Ni3Al Intermetallic Compound
نویسندگان
چکیده
Occupied sites by dopants of Ag(O.lat%). Pd(Zat%) and Zr(OAat%) in the Ni3AI intermetallic compound are investigated by means of EXAFS analysis. It is found that Pd substitutes the Ni site and Zr substitutes the A1 site. These results are consistent with tthose of channeling enhanced microanalysis. Ag is also determined to substitute in the Ni site by EXAFS and this result supports that Ag additive is y-phase(disorder phase) former. The expansion of the nearest neighbor distance around Ag, Pd and Z are 2%. 3% and 4% respectively.
منابع مشابه
An Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملInvestigating the Joining of Ni3Al Intermetallic Compound, using Transient Liquid Phase (TLP) Method with Cu Interlayer
In this study, joining of Ni3Al intermetallic compounds using the transient liquid phase (TLP) process with Cu interlayer was investigated. The binding process was carried out in a vacuum furnace at a temperature of 1050 °C for different times of 30, 60, 90 and 120 minutes. The effect of time variation on microstructure and mechanical properties of the joint zone was investigated. The EDS analy...
متن کاملAn Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملSynthesis and Characterization of Nanocrystalline Ni3Al Intermetallic during Mechanical Alloying Process
In this research, formation of nanocrystalline Ni3Al intermetallic from Ni and Al elemental powders by mechanical alloying (MA) process and its characterization was investigated. Therefore, the evolutions in microstructure such as phase transformation, oxidation in air and introduction of Fe impurity from milling media after MA were evaluated using XRD, Rietveld refinement, TEM, SEM, EDS and IC...
متن کاملANALYTICAL DATA FOR NiO REDUCTION AND Al3Ni2 INTERMETALLIC COMPOUND FORMATION
In this research, the nickel oxide was dissolved in cryolite at temperatures of 880, 940 and 1000°C. In order to reduce the nickel oxide, aluminum was added to the salt. Simultaneously the nickel oxide was reduced and Al3Ni2 intermetallic compound was formed. In the duration intervals of 2.5-40 minutes samples of the salt and metallic phases were taken. The variation of the nickel content in me...
متن کامل