Using Iron-Manganese Co-Oxide Filter Film to Remove Ammonium from Surface Water
نویسندگان
چکیده
An iron-manganese co-oxide filter film (MeOx) has been proven to be a good catalyst for the chemical catalytic oxidation of ammonium in groundwater. Compared with groundwater, surface water is generally used more widely and has characteristics that make ammonium removal more difficult. In this study, MeOx was used to remove ammonium from surface water. It indicated that the average ammonium removal efficiency of MeOx was greater than 90%, even though the water quality changed dramatically and the water temperature was reduced to about 6-8 °C. Then, through inactivating microorganisms, it showed that the removal capability of MeOx included both biological (accounted for about 41.05%) and chemical catalytic oxidation and chemical catalytic oxidation (accounted for about 58.95%). The investigation of the characterizations suggested that MeOx was formed by abiotic ways and the main elements on the surface of MeOx were distributed homogenously. The analysis of the catalytic oxidation process indicated that ammonia nitrogen may interact with MeOx as both ammonia molecules and ammonium ions and the active species of O₂ were possibly •O and O₂-.
منابع مشابه
A comparison study of the start-up of a MnOx filter for catalytic oxidative removal of ammonium from groundwater and surface water.
As an efficient method for ammonium (NH4+) removal, contact catalytic oxidation technology has drawn much attention recently, due to its good low temperature resistance and short start-up period. Two identical filters were employed to compare the process for ammonium removal during the start-up period for ammonium removal in groundwater (Filter-N) and surface water (Filter-S) treatment. Two typ...
متن کاملThin Film Heterogeneous Ion Exchange Membranes Prepared by Interfacial Polymerization of PAA-co-Iron-Nickel Oxide Nanoparticles on Polyvinylchloride Based Substrate
In this research thin film heterogeneous cation exchange membrane was prepared by interfacial polymerization of polyacrylic acid-co-iron nickel oxide nanoparticle son PVC based substrate. Spectra analysis confirmed graft polymerization conclusively. The SEM images showed that polymerized layer covers the membranes by simple gel network entanglement. Results exhibited that membrane water content...
متن کاملCatalytic Decomposition of Hydrogen Peroxide in the Presence of Synthesized Iron-Manganese oxide Nanocomposites via Different Methods
The special application of iron-manganese oxide nanocatalysts has been investigated in decomposition of hydrogen peroxide. In this research, iron-manganese oxide nanocomposites were synthesized by co-precipitation, sol-gel and mechanochemical methods using iron (III) nitrate, iron (II) sulfate and manganese (II) nitrate as starting materials. These nanocomposites were prepared on the variou...
متن کاملRemoval of Fe2+ from Aqueous Solution Using Manganese Oxide Coated Zeolite and Iron Oxide Coated Zeolite
The adsorption of Fe2+ by the manganese oxide coated zeolite (MOCZ) and iron oxide coated zeolite (FOCZ) was studied. Surface properties of adsorbents have been investigated for monitoring their changes and morphology for both of the MOCZ and FOCZ. Main variables namely; contact time, pH, initial concentration of Fe2+, size and dosage of adsorbent have been optimized, and the results contrasted...
متن کاملInvestigation on Influences of Synthesis Methods on the Magnetic Properties of Trimetallic Nanoparticles of Iron-Cobalt-Manganese Supported by Magnesium Oxide
Using Fe(NO3)3.9H2O, Co(NO3)2.6H2O and Mn(NO3)2.4H2O the magnetic properties of nanoparticles trimetalic Iron - Cobalt - Manganese, with supported Magnesium oxide have been prepared by Co-precipitation and Solvothermal methods. The prepared samples are characterized by Scanning Electron Micros...
متن کامل