Investigations of the ex situ ionic conductivities at 30 degrees C of metal-cation-free quaternary ammonium alkaline anion-exchange membranes in static atmospheres of different relative humidities.
نویسنده
چکیده
This article presents the first systematic study of the effect of Relative Humidity (RH) on the water content and hydroxide ion conductivity of quaternary ammonium-based Alkaline Anion-Exchange Membranes (AAEMs). These AAEMs have been developed specifically for application in alkaline membrane fuel cells, where conductivities of >0.01 S cm(-1) are mandatory. When fully hydrated, an ETFE-based radiation-grafted AAEM exhibited a hydroxide ion conductivity of 0.030 +/- 0.005 S cm(-1) at 30 degrees C without additional incorporation of metal hydroxide salts; this is contrary to the previous wisdom that anion-exchange membranes are very low in ionic conductivity and represents a significant breakthrough for metal-cation-free alkaline ionomers. Desirably, this AAEM also showed increased dimensional stability on full hydration compared to a Nafion-115 proton-exchange membrane; this dimensional stability is further improved (with no concomitant reduction in ionic conductivity) with a commercial AAEM of similar density but containing additional cross-linking. However, all of the AAEMs evaluated in this study demonstrated unacceptably low conductivities when the humidity of the surrounding static atmospheres was reduced (RH = 33-91%); this highlights the requirement for continued AAEM development for operation in H(2)/air fuel cells with low humidity gas supplies. Preliminary investigations indicate that the activation energies for OH(-) conduction in these quaternary ammonium-based solid polymer electrolytes are typically 2-3 times higher than for H(+) conduction in acidic Nafion-115 at all humidities.
منابع مشابه
Polysulfone-based Anion Exchange Membranes for Potential Application in Solid Alkaline Fuel Cells
In present research work, anion exchange membranes based on quaternized polysulfone with ammonium cation moieties (QAPSF) were prepared by chloromethylation, amination and alkalization. The chloromethylated polysulfone were characterized by 1HNMR spectroscopy and functionalization degree was determined according to peak area integration. Ion transport properties (ionic conductivity, ion exchang...
متن کاملAlkaline Stability of Novel Aminated Polyphenylene-Based Polymers in Bipolar Membranes
This research investigated stability of two novel aminated polyphenylene polymers as anion exchange layers in bipolar membranes. Bipolar membrane stability was tested under operating conditions of 50 mA/cm2, and under conditions of soaking in room temperature 1 M NaOH. The stability of the custom made bipolar membranes was compared with those for two commercial membranes. For the polyphenylene-...
متن کاملPoly (Ether Ether Ketone) Based Anion Exchange Membrane for Solid Alkaline Fuel Cell: A Review
Solid alkaline fuel cell is employed by polymer anion exchange membrane (AEM) that is permeable to hydroxide ion. A number of polymers have been proposed for AEM which include polysulfone (PSF), poly (phenylene oxide) (PPO), and poly (ether ether ketone) (PEEK). The purpose of this paper was to conduct a critical review on the development of PEEK polymer as AEM, particu...
متن کاملReactive oxygen species accelerate degradation of anion exchange membranes based on polyphenylene oxide in alkaline environments.
Anion exchange membranes (AEM) based on polyphenylene oxide (PPO) suffered quaternary-ammonium-cation-site degradation in alkaline environments. Surprisingly, the degradation rate was considerably faster in the presence of molecular oxygen. We postulated that the AEM cation-site catalyzes the reduction of dioxygen by hydroxide ions to yield the superoxide anion radical and the highly reactive h...
متن کاملThermal Crosslinking of an Alkaline Anion Exchange Membrane Bearing Unsaturated Side Chains
We report a facile new route for the synthesis of self-crosslinked anion exchange membranes (AEM) without the need for any crosslinkers or catalysts. The soluble copolymers bearing flexible side chains, with alkene pendant groups, were synthesized via the Menshutkin reaction. The crosslinked derivatives were then prepared by the thermal crosslinking of the unsaturated side chains during the mem...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Physical chemistry chemical physics : PCCP
دوره 9 12 شماره
صفحات -
تاریخ انتشار 2007