Controlled synthesis of Co3O4 nanopolyhedrons and nanosheets at low temperature.
نویسندگان
چکیده
Cobalt oxide (Co(3)O(4)) nanopolyhedrons and nanosheets were controlled synthesized at the low temperature of 80 degrees C via a novel, simple, aqueous method; the obtained nanosheets are only 2-3 nm thick.
منابع مشابه
Synthesis of porous Co3O4 nanonetworks to detect toluene at low concentration.
Porous Co3O4 nanonetworks (NNWs), converted from precursor CoOOH nanosheets, have been synthesized via a controllable chemical reaction route followed by calcination at 400 °C in air. The morphologies and microstructures of the precursor nanosheets and the final products were characterized by high-resolution transmission electron microscopy and X-ray diffraction, respectively. The growth mechan...
متن کامل2D Porous ZnO Nanosheets: One Pot Synthesis with Low Turn-on Field
Low turn-on field of 2.3 V/µm was found for the emission current density of 10 µA/cm2 from 2D porous ZnO nanosheets. High current density of 0.76 mA/cm2 was drawn at an applied field of 4.1 V/µm. The observed low turn-on field of porous ZnO nanosheets has been found to be superior to the other ZnO nanostructures reported in the literature. Also, the emission current stability over a period of 3...
متن کاملNanoparticle Decorated Ultrathin Porous Nanosheets as Hierarchical Co3O4 Nanostructures for Lithium Ion Battery Anode Materials
We report a facile synthesis of a novel cobalt oxide (Co3O4) hierarchical nanostructure, in which crystalline core-amorphous shell Co3O4 nanoparticles with a bimodal size distribution are uniformly dispersed on ultrathin Co3O4 nanosheets. When tested as anode materials for lithium ion batteries, the as-prepared Co3O4 hierarchical electrodes delivered high lithium storage properties comparing to...
متن کاملElectrochemical Partial Reforming of Ethanol into Ethyl Acetate Using Ultrathin Co3O4 Nanosheets as a Highly Selective Anode Catalyst
Electrochemical partial reforming of organics provides an alternative strategy to produce valuable organic compounds while generating H2 under mild conditions. In this work, highly selective electrochemical reforming of ethanol into ethyl acetate is successfully achieved by using ultrathin Co3O4 nanosheets with exposed (111) facets as an anode catalyst. Those nanosheets were synthesized by a on...
متن کاملCharacterization of Cobalt Oxide Co3O4 Nanoparticles Prepared by Various Methods: Effect of Calcination Temperatures on Size, Dimension and Catalytic Decomposition of Hydrogen Peroxide
In this scientific research work we report a novel method to synthesis Co3O4 nanoparticles via calcinations of cobalt hydroxide which can be conveniently prepared by the Co(NO3 )2.6H2O with different reactants. In order to study the effect of calcination temperature on structure and morphology of the nanoparticles, the calcinations take place at various temperatures (at 300°C, 500°C and 700°C)....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 48 شماره
صفحات -
تاریخ انتشار 2009