Comparison of frictional resistance between self-ligating and conventional brackets tied with elastomeric and metal ligature in orthodontic archwires

OBJECTIVE To compare the frictional resistance between self-ligating and conventional brackets tied to different types of wire. MATERIAL AND METHODS Abzil Kirium Capelozza (Pattern I) and Easy Clip (Roth prescription) incisor brackets were used. An elastomeric ligature or a 0.10-in ligating wire was used to ligate the wire to the Abzil bracket. Three types of orthodontic archwire alloys were assessed: 0.016-in NiTi wire, 0.016 x 0.021-in NiTi wire and 0.019 x 0.025-in steel wire. Ten observations were carried out for each bracket-archwire angulation combination. Brackets were mounted in a special appliance, positioned at 90 degrees in relation to the wire and tested in two angulations. Frictional test was performed in a Universal Testing Machine at 5 mm/min and 10 mm of displacement. The means (MPa) were submitted to ANOVA and Tukey's test set at 5% of significance. The surfaces of wires and brackets were observed at SEM. RESULTS Steel-tied brackets (16.48 ± 8.31) showed higher means of frictional resistance than elastomeric-tied brackets (4.29 ± 2.16 ) and self-ligating brackets (1.66 ± 1.57) (P < 0.05), which also differed from each other (P < 0.05). As for the type of wire, 0.019 x 0.025-in steel wire (5.67 ± 3.97) showed lower means (P < 0.05) than 0.16-in NiTi wire (8.26 ± 10.92) and 0.016 x 0.021-in NiTi wire (8.51 ± 7.95), which did not differ from each other (P > 0.05). No statistical differences (P > 0.05) were found between zero (7.76 ± 8.46) and five-degree (7.19 ± 7.93) angulations. CONCLUSIONS Friction was influenced not only by the type of bracket, but also by the ligating systems. Different morphological aspects were observed for the brackets and wires studied.