Fabrication and Optoelectronic properties of Fluoride tin oxides/porous silicon/p-Silicon heterojunction
نویسنده
چکیده
In this paper, formation of a nanostructure semi transparence fluoride tin oxides (FTO) by spray pyrolysis technique on porous silicon PS layer. Porous silicon PS layer was prepared by anodization of p-type silicon wafers to fabricate of the UVVisible Fluoride-doped tin oxide /Porous silicon /p-Si heterojunction photodetector. Optical properties of FTO thin films were measured. The optical band gap of 3.77 eV for SnO2: Ffilm was deduced. From (I-V) and (C-V) measurements, the barrier height ∅B for FTO/PS diode was of 0.77 eV, and the built in voltage Vbi, which was of 0.95 V. External quantum efficiency was 55 % at 500 nm which corresponding to peak responsivity of 1.15 A/W at 1 V bias. The PS band gap in the vicinity of PS/c-Si heterojunction was 1.38 eV.
منابع مشابه
Influence of current density on refractive index of p-type nanocrystalline porous silicon
Porous Silicon (PS) layers have been prepared from p-type silicon wafers of (100) orientation. SEM, XRD, FTIR and PL studies were done to characterize the surface morphological and optical properties of PS. The porosity of the PS samples was determined using the parameters obtained from SEM images by geometric method. The refractive index values of the PS samples as a function of poros...
متن کاملFabrication of p-Type Nano-porous Silicon Prepared by Electrochemical Etching Technique in HF-Ethanol and HF-Ethanol-H2O Solutions
Nano-porous silicon were simply prepared from p-type single crystalline silicon wafer by electrochemical etching technique via exerting constant current density in two different HF-Ethanol and HF-Ethanol-H2O solutions. The mesoporous silicon layers were characterized by field emission scanning electron microscopy and scanning electron microscopy. The results demonstrate that the width of nano-p...
متن کاملInfluence of current density on refractive index of p-type nanocrystalline porous silicon
Porous Silicon (PS) layers have been prepared from p-type silicon wafers of (100) orientation. SEM, XRD, FTIR and PL studies were done to characterize the surface morphological and optical properties of PS. The porosity of the PS samples was determined using the parameters obtained from SEM images by geometric method. The refractive index values of the PS samples as a function of poros...
متن کاملHydrogen-doped indium oxide/indium tin oxide bilayers for high-efficiency silicon heterojunction solar cells
The front transparent conductive oxide layer is a source of significant optical and electrical losses in silicon heterojunction solar cells because of the trade-off between free-carrier absorption and sheet resistance. We demonstrate that hydrogen-doped indium oxide (IO:H), which has an electron mobility of over 100 cm/V s, reduces these losses compared to traditional, low-mobility transparent ...
متن کاملFabrication and Optical Characterization of Silicon Nanostructure Arrays by Laser Interference Lithography and Metal-Assisted Chemical Etching
In this paper metal-assisted chemical etching has been applied to pattern porous silicon regions and silicon nanohole arrays in submicron period simply by using positive photoresist as a mask layer. In order to define silicon nanostructures, Metal-assisted chemical etching (MaCE) was carried out with silver catalyst. Provided solution (or materiel) in combination with laser interference lithogr...