Surface Roughness of Composite Panels as a Quality Control Tool
نویسنده
چکیده
This paper describes a study of the quantify surface roughness of experimentally manufactured particleboards and sandwiched panels having fibers on the surface layers. Surface quality of specimens before and after being overlaid with thin melamine impregnated papers was determined by employing profilometer equipment. Roughness measurements and Janka hardness were carried out on the specimens conditioned at 60% and 95% relative humidity levels. Based on the findings in this work, surface roughness of the specimens that were exposed two relative humidity exposure showed significant differences from each others. Data determined in this study could be beneficial to understand behavior of such panels exposed different humidity levels.
منابع مشابه
In-Vitro Comparative Study of the Effect of Four Finishing and Polishing Tools on Surface Roughness of a Microhybrid Resin Composite
Background and Aim: The complications of unwanted surface roughness of composite restorations are highly common due to the increasing use of this restorative material. Therefore, the present study was designed to compare the effect of four finishing and polishing (F&P) tools on surface roughness of microhybrid resin composites. Materials and Methods: This experimental study was performed on 42...
متن کاملStudy on tool wear and surface roughness in end milling of particulate aluminum metal matrix composite: Application of response surface methodology
Metal matrix composites have been widely used in industries, especially aerospace industries, due to their excellent engineering properties. However, it is difficult to machine them because of the hardness and abrasive nature of reinforcement elements like silicon carbide particles (SiCp).In the present study, an attempt has been made to investigate the influence of spindle speed (N), feed rate...
متن کاملInvestigation the Milling Strategies Effects on Machining of Convex Surfaces made of Glass/Epoxy Composite
In this study the effects of machining parameters such as shearing speed, feed rate, tool diameter and machining depth on different milling strategies i.e. 3D offset, spiral, raster and radial to produce the convex surface made of epoxy/glass composites is investigated. The effects of mentioned strategies on output parameters such as surface roughness and milling removal rate is also studied. T...
متن کاملComparative Evaluation of Surface Roughness of Three Different Composite Resins Following Polishing with a Two-Step Technique
Background and Aim: Nowadays, demand for same–color restorative materials, especially resin composites, is increasing. Access to the smooth surface with minimum level of surface roughness significantly results in more beauty, and the reduction of the accumulation of the plaque, gingival inflammation, and tooth discoloration. the aim of this study was surface roughness of three different composi...
متن کاملEffect of Fire Retardants on Surface Roughness and Wettability of Wood Plastic Composite Panels
Surface roughness and wettability of flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) (5, 10, or 15% by weight (wt)) at 50 wt-% content of the wood flour (WF) were investigated. The most common FRs, zinc borate (ZB), magnesium hydroxide (MH), and ammonium polyphosphate (APP), were used in the experiments. The WPC panels were made from dry-blended wood ...
متن کامل