The mechanism of texture formation during film growth: The roles of preferential sputtering and shadowing
نویسندگان
چکیده
Nonequilibrium molecular dynamics simulations have been employed to develop a mechanistic model for the development of an out-of-plane ~fiber! texture in polycrystalline thin films. The depositing atoms preferentially sputter film atoms from grains with high surface energies. As the film grows, an atomic shadowing mechanism leads to the lateral growth of the grains with a height advantage—eventually leading to the occlusion of randomly oriented grains. © 1996 American Institute of Physics. @S0003-6951~96!01246-6#
منابع مشابه
Effect of Thickness on Properties of Copper Thin Films Growth on Glass by DC Planar Magnetron Sputtering
Copper thin films with nano-scale structure have numerous applications in modern technology. In this work, Cu thin films with different thicknesses from 50–220 nm have been deposited on glass substrate by DC magnetron sputtering technique at room temperature in pure Ar gas. The sputtering time was considered in 4, 8, 12 and 16 min, respectively. The thickness effect on the structural, mo...
متن کاملEffect of magnetron sputtering parameters and stress state of W film precursors on WSe2 layer texture by rapid selenization
Tungsten diselenide (WSe2) film was obtained by rapid selenization of magnetron sputtered tungsten (W) film. To prevent WSe2 film peeling off from the substrate during selenization, the W film was designed with a double-layer structure. The first layer was deposited at a high sputtering-gas pressure to form a loose structure, which can act as a buffer layer to release stresses caused by WSe2 gr...
متن کاملGrowth anisotropy and self-shadowing: A model for the development of in-plane texture during polycrystalline thin-film growth
The development of a preferred crystallographic orientation in the plane of growth, an in-plane texture, is addressed in a model that incorporates anisotropic growth rates of a material and self-shadowing. Most crystalline materials exhibit fast growth along certain crystallographic directions and slow growth along others. This crystallographic growth anisotropy, which may be due to differences...
متن کاملDry and Wet Wear Characteristic of TiO2 Thin Film Prepared by Magnetic Sputtering in Ringer Solution
In this research, a thin film of TiO2 was applied on AZ91D using the method of magnetic sputtering. Microstructure investigations were done using field emission scanning electron microscope (FESEM) and X-ray diffraction (XRD). Wear resistance for the coating was investigated using the pin on the disk in the form of dry and in the Ringer's solution. After this test, the worn surface of the sampl...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کامل