Shape Evolution of Layer-Structured Bismuth Oxychloride Nanostructures via Low-Temperature Chemical Vapor Transport
نویسندگان
چکیده
Chemistry of Materials is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Article Shape Evolution of Layer-Structured Bismuth Oxychloride Nanostructures via Low-Temperature Chemical Vapor Transport Hailin Peng, Candace K. Chan, Stefan Meister, Xiao Feng Zhang, and Yi Cui Chem. Mater., 2009, 21 (2), 247-252• DOI: 10.1021/cm802041g • Publication Date (Web): 19 December 2008 Downloaded from http://pubs.acs.org on April 24, 2009
منابع مشابه
Structural and electrical characterization of Bi₂Se₃ nanostructures grown by metal-organic chemical vapor deposition.
We characterize nanostructures of Bi(2)Se(3) that are grown via metal-organic chemical vapor deposition using the precursors diethyl selenium and trimethyl bismuth. By adjusting growth parameters, we obtain either single-crystalline ribbons up to 10 μm long or thin micrometer-sized platelets. Four-terminal resistance measurements yield a sample resistivity of 4 mΩ·cm. We observe weak antilocali...
متن کاملSynthesis of 2-D nanostructures of Bismuth Oxychloride
This project studies the synthesis process of 2-D nanostructure of inorganic materials. This project studies the ZnO thin layer deposition on a commercial grade paper using Atomic Layer Deposition (ALD) technique and its effectiveness of reducing water permeability. The experiment utilizes a commercial grade blue ink for the testing of the permeability. The purpose of the experiment is to succe...
متن کاملSynthesis and Thermoelectric Properties of Bi2Se3 Nanostructures
Bismuth selenide (Bi2Se3) nanostructures were synthesized via solvothermal method. The crystallinity of the as-synthesized sample has been analyzed by X-ray diffraction, which shows the formation of rhombohedral Bi2Se3. Electron microscopy examination indicates that the Bi2Se3 nanoparticles have hexagonal flake-like shape. The effect of the synthesis temperature on the morphology of the Bi2Se3 ...
متن کاملGreen Method for Synthesizing Gallium Nitride Nanostructures at Low Temperature
Gallium nitride (GaN) nanostructures (NS) were synthesized using pulseddirect current plasma enhanced chemical vapor deposition (PDC-PECVD) on quartzsubstrate at low temperature (600°C). Gallium metal (Ga) and nitrogen (N) plasma wereused as precursors. The morphology and structure of the grown GaN NS werecharacterized by field emission scanning electron microscope (FE-SEM), transmissionelectro...
متن کاملImproving Gas Sensing Properties of Tin Oxide Nanowires Palladium-Coated Using a Low Cost Technique
Thin films of SnO2 nanowires were successfully prepared by using chemical vapor deposition (CVD) process on quartz substrates. Afterwards, a thin layer of palladium (Pd) as a catalyst was coated on top of nanowires. For the deposition of Pd, a simple and low cost technique of spray pyrolysis was employed, which caused an intensive enhancement on the sensing response of fabricated sensors...