Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

نویسندگان

  • Jianfeng Dong
  • Yuxi Zhao
چکیده

This study investigated the chloride penetration of surface-treated concrete in natural and accelerated environments. A part of a real concrete port, including the beams and the columns, was investigated. Concrete specimens cast together with the concrete port were transported to the lab and subjected to wetting and drying cycles for accelerating the ingression of chloride ion. Chloride concentration of the specimens in the lab and the components in situ was tested. The results show that the surface treatments obviously slow down the chloride penetration into the concrete in both lab and in situ. The chloride penetration in situ is more severe than that in specimens under wetting and drying cycles. For the components of the real concrete port, the chloride concentration tested in summer is found higher than that in winter and the chloride concentration in the tensile region of bending beam is higher than that in the column.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Durable Glass Fiber Reinforced Concrete with Supplimentary Cementitious Materials

Durability of concrete structure in marine environments is a big issue for many decades due to chloride attack. Chloride penetrates the concrete structure and accelerates the corrosion process of reinforcement which decreases the life of those structures. Also shrinkage cracks in concrete play main role for chloride penetration through concrete surface.  Many researchers tried to find easy and ...

متن کامل

Durability of Self-compacting Lightweight Aggregate Concretes (LWSCC) as Repair Overlays

For rehabilitation of damaged concrete structures, the durability of repair overlay is a very important issue. Self-compacting concretes (SCC) are known as a suitable repair overlay materials. In this study, the durability of different self-compacting lightweight aggregate concretes (LWSCC) and effect of lightweight aggregate type on them is investigated. 3 mix designs of LWSCC containing three...

متن کامل

Time-Dependent Structural Behavior of Repaired Corroded RC Columns Located in a Marine Site

The chloride corrosion of reinforcing steel in reinforced concrete (RC) structures is a significant reason for premature deterioration and failure of RC structures in aggressive environments such as Persian Gulf region. This is one of the most important sources of engineering and economic problems in developed countries. So, the repair and maintenance of RC structures exposed to corrosive envir...

متن کامل

Exposure Test on Two Surface Anticorrosion Technologies for Marine Concrete Structure

This paper is to study the effect of surface coating and silane hydrophobic agents for high performance concrete durability in a marine environment of tidal zone and splash zone by exposure test in JiaoZhou Bay. The results indicated that surface coating had good protection and coating quality after a 5-year period and the adhesive strength with concrete surface was more than 2.5 MPa. Surface c...

متن کامل

Performance of High-strength Concrete Made with Recycled Ceramic Aggregates

Recent scientific concerns to achieve sustainability in construction have suggested the implementation of using recycled aggregate in concrete because it has the potential to reduce the demand for extraction of natural raw materials and decrease the volume of wastes landfilled. In this respect, this study aims to investigate the suitability of using ceramic tile (CT) and ceramic sanitary (CS) w...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2016