3D FEA Modelling of Laminated Composites in Bending and Their Failure Mechanisms
نویسندگان
چکیده
This paper developed three-dimensional (3D) Finite Element Analysis (FEA) to investigate the effect of fibre lay-up on the initiation of failure of laminated composites in bending. TsaiHill failure criterion was applied to identify the critical areas of failure in composite laminates. In accordance with the 3D FEA, unidirectional ([0]16), cross-ply ([0/90]4s) and angle-ply ([±45]4s) laminates made up of pre-preg Carbon Fibre Reinforced Plastics (CFRP) composites were manufactured and tested under three-point bending. The basic principles of Classical Laminate Theory (CLT) were extended to three-dimension, and the analytical solution was critically compared with the FEA results. The 3D FEA results revealed significant transverse normal stresses in the cross-ply laminate and in-plane shear stress in the angle-ply laminate near free edge regions which are overlooked by conventional laminate model. The microscopic images showed that these free edge effects were the main reason for stiffness reduction observed in the bending tests. The study illustrated the significant effects of fibre lay-up on the flexural failure mechanisms in composite laminates which lead to some suggestions to improve the design of composite laminates.
منابع مشابه
3d Woven Composites for Energy Absorbing Applications
Due to the presence of through-thickness reinforcement, 3D woven composites have superior fracture toughness, fatigue life, and damage tolerance compared to laminated composites. Furthermore, 3D woven composites exhibit a progressive damage behavior which is more benign than the typical catastrophic failure behavior of laminated composites. These properties lead to high specific energy absorpti...
متن کاملProgressive Damage Analysis of Laminated Composites using Continuum Damage Mechanics
In this paper, progressive damage and global failure of composite laminates under quasi-static, monotonic loading are investigated using 3D continuum damage mechanics. For this purpose, a finite element program has been developed using an eight-node 2D layered element including layer-wise plate theory. Damage analysis of a single orthotropic layer under various uniform in-plane and transverse l...
متن کاملMulti-scale modelling of moisture diffusion coupled with stress distribution in CFRP laminated composites
Laminated composite structures operating in a marine environment are subject to moisture ingress. Due to the slow diffusion process of moisture, the distribution of moisture is not uniform so that the laminates can develop hygrothermal stresses. An accurate prediction of the moisture concentration and the associated hygrothermal stress is vital to the understanding of the effect of marine envir...
متن کاملA Numerical and Analytical Solution for the Free Vibration of Laminated Composites Using Different Plate Theories
An analytical and numerical solution for the free vibration of laminated polymeric composite plates with different layups is studied in this paper. The governing equations of the laminated composite plates are derived from the classical laminated plate theory (CLPT) and the first-order shear deformation plate theory (FSDT). General layups are evaluated by the assumption of cross-ply and angle-p...
متن کاملDelamination Analysis in Composite Root of a Carbon-Layer Reinforced Wind Turbine Blade
The inconsistencies accompanied with material properties tipically cause the rise of delamination risk in composites made of different types of glass and crabon fibers. In this study, the delamination of a composite beam reinforced with a carbon layer under bending load is investigated. To this end, a small piece of a wind turbine blade root in the form of a heterogeneous laminated plate is sim...
متن کامل