Presentation of a novel model of chitosan- polyethylene oxide-nanohydroxyapatite nanofibers together with bone marrow stromal cells to repair and improve minor bone defects

OBJECTIVES Various methods for repairing bone defects are presented. Cell therapy is one of these methods. Bone marrow stromal cells (BMSCs) seem to be suitable for this purpose. On the other hand, lots of biomaterials are used to improve and repair the defect in the body, so in this study we tried to produce a similar structure to the bone by the chitosan and hydroxyapatite. MATERIALS AND METHODS In this study, the solution of chitosan-nanohydroxyapatite-polyethylene oxide (PEO) Nanofibers was produced by electrospinning method, and then the BMSCs were cultured on this solution. A piece of chitosan-nanohydroxyapatite Nanofibers with BMSCs was placed in a hole with the diameter of 1 mm at the distal epiphysis of the rat femur. Then the biomechanical and radiographic studies were performed. RESULTS Biomechanical testing results showed that bone strength was significantly higher in the Nanofiber/BMSCs group in comparison with control group. Also the bone strength in nanofiber/BMSCs group was significant, but in nanofiber group was nearly significant. Radiographic studies also showed that the average amount of callus formation (radio opacity) in nanofiber and control group was not significantly different. The callus formation in nanofiber/BMSCs group was increased compared to the control group, and it was not significant in the nanofiber group. CONCLUSION Since chitosan-nanohydroxyapatite nanofibers with BMSCs increases the rate of bone repair, the obtained cell-nanoscaffold shell can be used in tissue engineering and cell therapy, especially for bone defects.