Tie-Line Compositions of the and ( ; ) Phases in the Re-Cr-Ni System at 1573K*
نویسندگان
چکیده
Compositions with tie lines between the and ( ; ) phases in a ternary Re-Cr-Ni system were investigated by heat treating various ternary Re-Cr-Ni alloys at 1573K in vacuum for up to 2000 h. The microstructures of the Re-containing alloys that had been water quenched after various heat treatment for times were observed and their concentration profiles for Re, Cr, and Ni were measured using an electron probe microanalyzer. The Re-Cr-Ni alloys consisted of the phase with either the or phase. The concentration profiles of the phase became flat after short heat treatment, whereas longer times of up to 2000 h were required to achieve the same effect for the and phases. The tie-line composition (at%) of each phase at 1573K was experimentally determined as follows. The phase tie-line with the phase (17.3 Re, 20.6 Cr, and 62.1 Ni) consists of 53.1 Re, 25.5 Cr, and 21.4 Ni. The phase tie-lined with the phase (16.9 Re, 19.2 Cr, and 63.9 Ni) consists of 53.0 Re, 24.6 Cr, and 22.4 Ni. The phase tie-line with the phase (12.7 Re, 24.8 Cr, and 62.5 Ni) consists of 48.4 Re, 30.9 Cr, and 20.7 Ni. The phase tie-line with the phase (6.1 Re, 46.2 Cr, and 47.7 Ni) consists of 28.1 Re, 52.3 Cr, and 19.6 Ni. The phase tie-line with the phase (85.6 Re, 5.2 Cr, and 9.2 Ni) consists of 61.1 Re, 27.7 Cr, and 11.2 Ni. [doi:10.2320/matertrans.M2011206]
منابع مشابه
lactic acid extraction from aqueous solutions with 2-Ethyl-1-hexanol by using experimental liquid-liquid equilibrium data at T=298.2K and atmospheric pressure
Liquid-Liquid equilibrium data for the (water + Lactic acid + 2-ethy-1-hexanol) ternary system in T=298.2K and P=1atm were determined and tie- lines related to equilibrium data has been drawn in the phases diagram . The reliability of the experimental tie-line data for this system was as confirmed by using the Hand and Othmer –Tobias correlations. The tie-line data were correlated by means of t...
متن کاملPhase Equilibria of the Ternary System Water + Phosphoric Acid + 1-Nonanol at Different Temperatures
The purpose of this reaserch is to measure the phase equilibrium data of the ternary system (water + phosphoric acid + 1-nonanol) at different temperatures. Experimental solubility curves and tie-line points for the system were obtained at T = 298.2, 308.2 and 318.2 K and ambient pressure. The binodal curve data were detected by the cloud point method. The mass fractions of each layer ...
متن کاملEffect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
متن کاملEffect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
متن کاملLarge supercooled liquid region and phase separation in the Zr–Ti–Ni–Cu–Be bulk metallic glasses
Results of calorimetric, differential thermal analysis, and structural measurements are presented for a series of bulk metallic glass forming compositions in the Zr–Ti–Cu–Ni–Be alloy system. The calorimetric data for five alloys, prepared along the tie line between phase separating and nonphase separating compositions, show that the transition from phase separating to nonphase separating behavi...
متن کامل