Solubility and kinetic properties of deuterium in single crystal Pd
نویسندگان
چکیده
The pressure–composition (PC) behavior of deuterium in single crystal Pd has been measured over a temperature range extending from room temperature to 393 K. These data allow the determination of (i) relative partial molar enthalpy and entropy, without the contribution of the configuration entropy, for the dilute solid solution phase, (ii) enthalpy and entropy change characterizing the a→a9 phase transformation, and (iii) Gibbs free energy loss associated with the PC thermodynamic hysteresis. Comparison of these quantities with published data for polycrystal Pd and with our own polycrystal Pd measurements show good agreement, indicating grain boundary interfaces and second phase inclusions known to exist in polycrystalline Pd do not influence these thermodynamic properties. The time dependence of deuterium absorption and desorption from the gas phase has been measured in both single and polycrystal Pd as well. The activation energy and diffusion constant of deuterium in the solid solution phase of Pd agree with published values. The time dependence of deuterium absorption and desorption within the miscibility gap are reduced by approximately two orders of magnitude compared to solid solution behavior. The two-phase kinetic data exhibit an Arrhenius behavior with a factor of two increase in the activation energy compared to diffusion. This is attributed to the phase transformation process controlling the deuterium absorption /desorption kinetic behavior when the Pd–D system is within the miscibility gap. 2000 Elsevier Science B.V. All rights reserved.
منابع مشابه
SANS measurements of deuteride ( hydride ) formation in single crystal Pd
In situ small-angle neutron scattering (SANS) measurements of deuteride precipitation in well-annealed, undeformed single crystal Pd have been performed at room temperature to observe the morphology of the precipitate as the deuterium fraction was increased over a range of 0.005 to 0.097 [D] / [Pd]. Supporting measurements were made of the room temperature deuterium solubility isotherm in the s...
متن کاملCarboxypeptidasey from Saccharomyces cerevisiae Conformational Difference Reflected in Kinetic Behaviour in Water and Deuterium Oxide
متن کامل
Metallurgical characterization of Pd electrodes employed in calorimetric experiments under electrochemical deuterium loading
A systematic approach has been followed in the production and characterization of Pd foils to be used in excess heat production experiments [1][ 2] . Starting with a metal foil as supplied, palladium samples have been fabricated and characterized in a step by step process, and then subjected to electrolysis deuterium loading. The characterized metallurgical properties include the main grain siz...
متن کاملDesign of Endlessly Single Mode Photonic Crystal Fibers with Desirable Properties using HC-EDA Algorithm
In this article, Hill Climbing (HC) and Estimation of Distribution Algorithm (EDA) are integrated to produce a hybrid intelligent algorithm for design of endlessly Single Mode Photonic Crystal Fibers (SMPCFs) structure with desired properties over the C communication band. In order to analyzing the fiber components, Finite Difference Frequency Domain (FDFD) solver is applied. In addition, a spe...
متن کاملEvaluating the Effect of Ta/W Ratio on Microstructure and Stress Rupture Properties of Ni-Based Single Crystal Superalloy PWA1483
In this study, the effect of Ta/W ratio on the microstructure and stress rupture properties of Ni-based single crystal (SX) superalloy PWA1483 was investigated. For this purpose, single crystal (SX) superalloys with different Ta/W ratios (0.75, 1.0, 1.32 and 1.5 in wt.%) were fabricated. The alloys were directionally solidified by Bridgman method under the same solidification condition at withd...
متن کامل