Comparison of bond strength of different endodontic sealers to root dentin: An in vitro push-out test
نویسندگان
چکیده
AIM To compare the bond strength of four different endodontic sealers to root dentin through push-out test design. MATERIALS AND METHODS Forty single-rooted teeth with completely formed apices were selected. Teeth were decoronated, and working length was determined. Instrumentation and irrigation were performed. The teeth were divided into four groups based upon the sealer used. Group 1: Bioceramic sealer (Endosequence), Group 2: Mineral trioxide aggregate (MTA) based sealer (MTA Fill apex), Group 3: Epoxy resin based sealer (MM-Seal), and Group 4: Dual cure resin-based sealer (Hybrid Root Seal). Manipulation and application of the sealer was done as per the manufacturer instructions. All the teeth were obturated using 6% gutta-percha. After obturation, each tooth was prepared for push-out test with root slices of 2 mm thickness using universal testing machine. RESULTS The highest bond strength was found in Group 1 (Endosequence) (P < 0.05) compared to other groups. The lowest bond strength was found in Group 2 (MTA Fill apex). Statistical analysis is done by two-way ANOVA and Newman-Keuls multiple post hoc. CONCLUSION The push-out bond strength of Bioceramic sealer was highest followed by resin-based sealer and lowest bond strength was observed in MTA-based sealer.
منابع مشابه
An investigation on the adhesion of two endodontic sealers AH 26, Dorifill) to dentin (
An investigation on the adhesion of two endodontic sealers AH 26, Dorifill) to dentin ( * - Dr. S. Khedmat** Dr. M. Khorramdoost*- Assistant professor of Endodontics Dept. Faculty of Dentistry Tehran University of Medical Sciences. ** - Dentist. Background and aim: Tensile bond strength of endodontic sealers to dentin is an indicative of sealer's adhesion to dentin. Due to the fact that Gutta...
متن کاملPush-out bond strength of different endodontic obturation material at three different sites - In-vitro study
BACKGROUND The key to success of any root canal therapy is adequate obturation of the prepared root canal space. Root canal sealers are not dimensionally stable and might dissolve partially over a period of time. The objective of this in vitro study is to evaluate the push-out bond strength to intraradicular dentin of two endodontic obturation materials. MATERIAL AND METHODS Forty extracted s...
متن کاملEffects of different intra canal medicaments on the push out bond strength of endodontic sealers
BACKGROUND One of the essential properties of the root canal sealers is the adhesion to root canal dentin and their higher bond strength decreases the microleakage. The aim of the present study was to compare the effect of Different Intracanal medicaments on the push out bond strength of AH26 and MTA Fillapex sealers. MATERIAL AND METHODS A total of 104 one-rooted extracted human teeth were d...
متن کاملBond strength of different endodontic sealers to dentin: push-out test
OBJECTIVE The aim of this in vitro study was to evaluate the bond strength of different root canal sealers to dentin. MATERIAL AND METHODS Forty extracted single-rooted human teeth were examined and the coronal and middle thirds of the canals were prepared with a 1.50 mm post drill (FibreKor Post System, Pentron). The teeth were allocated in two experimental groups, irrigated with 2.5% NaOCl+...
متن کاملThe Effect of BC Sealer, AH-Plus and Dorifill on Push-out Bond Strength of Fiber Post
Introduction Dentinal canal walls are in direct contact with endodontic sealers prior to post space preparation and luting cements after post space preparation. This direct contact may affect the bond strength of intraradicular posts to root dentin. This study aimed to assess the effect of three different sealers on the bond strength of fiber posts to root dentin. Methods and Materials The ca...
متن کامل