Noise characteristics and detectivity of YBa2Cu3O7 superconducting bolometers: Bias current, frequency, and temperature dependence

Meander line patterned infrared detectors, with values of resistance Ronset at the onset temperature Tc onset of 3–5 kV, were fabricated from YBa2Cu3O72x superconducting material on MgO and SrTiO3 crystalline substrates. Noise voltages from the samples were measured versus bias current, radiation modulation frequency, and temperature, in both the normal and superconducting states. Four major types of voltage noise were identified according to where they occurred in temperature relative to Tc onset and the zero resistance temperature Tc zero , and their dependence on frequency and bias current. They were also associated with the granularity of the superconducting film, which is related to the substrate material used. From these observations a specific cause for each type of noise is suggested. The results are as follows. ~i! In the normal state with temperature T . Tc onset , noise with a magnitude that is consistent with thermal ~Johnson! noise is seen, but it depends linearly on bias current above a threshold value, at low frequencies. The suggested noise source is conductivity fluctuations due to Cooper pairs. ~ii! Noise was found to occur below Tc zero in granular films. With increasing bias current its magnitude increases, and it shifts to a lower temperature range; however, the noise magnitude becomes constant as the current goes to zero. It is weakly dependent on frequency above 400 Hz. Suggested cause is voltage fluctuations in superconductor–normal–superconductor junctions at grain boundaries. ~iii! This noise also occurs below Tc zero with peaks at various temperatures. With increasing bias current the peaked noise spreads to lower temperatures, but the noise goes to zero as the bias current goes to zero. Its suggested cause is magnetic flux tube motion. ~iv! This noise occurs between Tc onset and Tc zero and is present in all samples, but lowest on samples prepared on SrTiO3 substrates. Its suggested cause is fluctuations in the volume fraction of the superconducting phase along the current path. While the measured detectivity D* of our samples at a wavelength of 20 mm was only 10 cm Hz/W, engineering changes can be expected to raise the value to above 10 cm Hz/W. © 1996 American Institute of Physics. @S0021-8979~96!03904-8#