Effects of V and Cr on Laser Cladded Fe-Based Coatings
نویسندگان
چکیده
Fe-based coatings with high V and Cr content were obtained by laser cladding using Fe-based powder with different Cr3C2 and FeV50 content. The results showed that Fe-based coatings were uniform and dense. The constituent phases were mainly composed of α-Fe solid solution with the increase of Cr3C2 and FeV50, γ-Fe and V8C7 phases were achieved. The microstructure of the coatings exhibited a typical dendrite structure. The concentration of C, V and Cr were saturated in dendritic areas, and the other alloying elements were mainly dissolved in the interdendritic areas. The hardness and wear resistance of Fe-based coatings were enhanced with the Cr3C2 and FeV50 addition. The specimen with 15% Cr3C2 and 16% FeV50 had the highest hardness of 66.1 ± 0.6 HRC, which was 1.05 times higher than the sample with 4.5% Cr3C2 and 5% FeV50, and the wear resistance of the former was three times greater than the latter.
منابع مشابه
Microstructure and Antiwear Property of Laser Cladding Ni–Co Duplex Coating on Copper
Ni-Co duplex coatings were cladded onto Cu to improve the antiwear properties of Cu products. Prior to laser cladding, n-Al₂O₃/Ni layers were introduced as interlayers between laser cladding coatings and Cu substrates to improve the laser absorptivity of these substrates and ensure defect-free laser cladding coatings. The structure and morphology of the coatings were characterized by scanning e...
متن کاملEffects of Different Levels of Boron on Microstructure and Hardness of CoCrFeNiAlxCu0.7Si0.1By High-Entropy Alloy Coatings by Laser Cladding
High-entropy alloys (HEAs) are novel solid solution strengthening metallic materials, some of which show attractive mechanical properties. This paper aims to reveal the effect of adding small atomic boron on the interstitial solid solution strengthening ability in the laser cladded CoCrFeNiAlxCu0.7Si0.1By (x = 0.3, x = 2.3, and 0.3 ≤ y ≤ 0.6) HEA coatings. The results show that laser rapid soli...
متن کاملMetallurgical and mechanical properties of laser cladded AlFeCuCrCoNi-WC10 high entropy alloy coating
In spite of excellent corrosion resistance, good ductility and low cost of AISI 316 austenitic stainless steel, the low hardness and poor mechanical charecteristic of material restricts its applicability in several industrial services. To improve upon mechanical properties AlFeCuCrCoNi-WC10 high-entropy alloy coatings were deposited via laser cladding on austentic stainless steel AISI 316 subst...
متن کاملSLURRY EROSION RESISTANCE OF LASER CLAD Fe–Cr–B–Si COATINGS
The slurry erosion behaviour of laser clad Fe–Cr–B–Si alloy coatings was investigated at impact angles from 30u to 90u with an increment of 15u, and compared with the slurry erosion behaviour of two laser clad carbide coatings and a non-coated substrate made of AISI 4140 steel. The Fe–Cr–B–Si alloy coatings had slurry erosion resistance. Their overall slurry erosion resistance at impact angles ...
متن کاملMicro-Structures and High-Temperature Friction-Wear Performances of Laser Cladded Cr–Ni Coatings
Cr-Ni coatings with the mass ratios of 17% Cr-83% Ni, 20% Cr-80% Ni and 24% Cr-76% Ni were fabricated on H13 hot work mould steel using a laser cladding (LC). The surface-interface morphologies, chemical elements, surface roughness and phase composition of the obtained Cr-Ni coatings were analysed using a scanning electron microscope (SEM), energy disperse spectroscopy (EDS), atomic force micro...