Dicyclopentadiene Hydroformylation to Value-Added Fine Chemicals over Magnetically Separable Fe3O4-Supported Co-Rh Bimetallic Catalysts: Effects of Cobalt Loading
نویسندگان
چکیده
Six Co-Rh/Fe3O4 catalysts with different cobalt loadings were prepared by the co-precipitation of RhCl3, Co(NO3)2, and Fe(NO3)3 using Na2CO3 as the precipitant. These catalysts were tested for dicyclopentadiene (DCPD) hydroformylation to monoformyltricyclodecenes (MFTD) and diformyltricyclodecanes (DFTD). The results showed that the MFTD formation rate increased with increasing cobalt loading, whereas the DFTD formation rate initially increased and then decreased when the cobalt loading was greater than twice that of Rh. The DFTD selectivity was only 21.3% when monometallic Rh/Fe3O4 was used as the catalyst. In contrast, the selectivity was 90.6% at a similar DCPD conversion when the bimetallic 4Co-2Rh/Fe3O4 catalyst was employed. These catalysts were characterized by temperature-programmed reduction (TPR), temperature-programmed desorption (TPD), and thermogravimetric and differential thermal analyses (TG-DTA). The results obtained by these complimentary characterization techniques indicated that adding cobalt to the Rh/Fe3O4 catalyst enhanced the Rh reducibility and dispersion; the Rh reducibility was easily altered, and increasing the cobalt loading improved the Rh dispersion. It was concluded that the enhanced catalytic performance with increasing cobalt loading might be due to the formation of a more reactive Rh species with a different Rh–phosphine interaction strength on the catalyst surface.
منابع مشابه
Atomic-level insights in optimizing reaction paths for hydroformylation reaction over Rh/CoO single-atom catalyst
Rh-based heterogeneous catalysts generally have limited selectivity relative to their homogeneous counterparts in hydroformylation reactions despite of the convenience of catalyst separation in heterogeneous catalysis. Here, we develop CoO-supported Rh single-atom catalysts (Rh/CoO) with remarkable activity and selectivity towards propene hydroformylation. By increasing Rh mass loading, isolate...
متن کاملSynthesis of MWCNTs Using Monometallic and Bimetallic Combinations of Fe, Co and Ni Catalysts Supported on Nanometric SiC via TCVD
Nanometric Carbid Silicon (SiC) supported monometallic and bimetallic catalysts containing Fe, Co, Ni transition metals were prepared by wet impregnation method. Multiwall carbon nanotubes (MWCNTs) were synthesized over the prepared catalysts from catalytic decomposition of acetylene at 850°C by thermal chemical vapor deposition (TCVD) technique. The synthesized nanomaterials (catalysts and CNT...
متن کاملCobalt Loading Effects on the Structure and Activity for Fischer-Tropsch and Water-Gas Shift Reactions of Co/Al2O3 Catalysts
An extensive study of Fischer-Tropsch synthesis (FTS) on alumina-supported cobalt catalysts with different amounts of cobalt is reported. Up to 40 wt % of cobalt, is added to the catalysts by impregnation method. The effect of the cobalt loading on the reducibility of the cobalt oxide species, dispersion of the cobalt, average clusters size, water-gas shift (WGS) activity and activity and s...
متن کاملCatalytic Oxidation of Carbon Monoxide by Cobalt Oxide Catalysts Supported on Oxidized-MWCNT
Cobalt oxide catalysts supported on oxidized multi-walled carbon nanotubes (MWCNT) for the low-temperature catalytic oxidation of carbon monoxide were prepared by an impregnation-ultrasound method. These catalysts were characterized by N2 adsorption/desorption, TEM, XRD, Raman, and H2-TPR methods. The XRD and Raman results indicated that the phase of the synthesized cobalt...
متن کاملFe3O4/FDU-12: A highly efficient and magnetically separable nano-catalyst for oxidation of alcohols
A series of Fe3O4 supported on mesoporous FDU-12 silica systems were prepared by the hydrothermal conditions. The surface properties of the functionalized catalyst were analyzed by a series of characterization techniques like FTIR, XRD, N2 adsorption–desorption and TEM. XRD and adsorption–desorption analysis shows that the mesostructure of FDU silica remains intact after Fe3O4 modifications, wh...
متن کامل